Contribution to the problem of the corrosion of lead in the building industryThe corrosion resistance of lead in mortar can be improved by surface treatment. The best protection is obtained with a chromate layer, followed by phosphate and the sulphate layers. The corrosion resistance of the protective layers is consistently superior when the mill scale on the lead sheet is removed by pickling prior to immersion into the treating solutions. While the useful life of a lead sheet (2.6 mm thick) without surface treatment is about 58 months in lime mortar and 43 months in cement mortar, the respective values for chromated sheets are 147 and 116 months.
Notes:
Die Korrosionsbeständigkeit von Blei in Mörtel kann durch Oberflächenbehandlung verbessert werden. Den besten Schutz bietet eine Chromatierungschicht, etwas schlechter ist eine Phosphatierungsschicht, und die geringste Schutzwirkung besitzt die Sulfatschicht. Der Korrosionswiderstand der Schutzschichten ist immer dann höher, wenn die Walzhaut des Bleibleches vor dem Eintauchen in die deckschichtbildenden Lösungen durch Ätzen entfernt wird. Während die Lebensdauer eines Bleiblechs von 2,6 mm Dicke ohne Oberflächenbehandlung in Kalkmörtel etwa 43 Monate beträgt, liegt sie im Falle der chromatierten Bleche bei 147 bzw. 166 Monaten.
Additional Material:
1 Tab.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19690200108