Description:
Radiation effects on engineering properties, dimensional stability, and chemistry on state of the art composite systems were characterized. T300/934 graphite-epoxy composite was subjected to 1.0 MeV electron radiation for a total dose of 1.0 x 10(10) rads at a rate of 5.0 x 10(7) rads/hour. This simulates a worst case exposure equivalent to 30 years in space. Mechanical testing was performed on he 4-ply unidirectional laminates over the temperature range of -250 F (116K) to +250 F (394K). A complete set of in-plane tensile elastic and strength properties were obtained (E sub 1, E sub 2, nu sub 12, G sub 12, X sub T, Y sub T, and S). In addition electron microscopy was used to study and analyze the fracture surfaces of all specimens tested. Results indicate that little difference in properties is noted at room temperature, but significant differences are observed at both low and elevated temperatures.
Keywords:
COMPOSITE MATERIALS
Type:
NASA-TM-85478
,
NAS 1.15:85478
,
CCMS-84-08
,
VPI-E-84-20
,
IR-45
Format:
application/pdf
Permalink