ISSN:
0887-624X
Keywords:
liquid crystalline
;
liquid crystal polymer
;
liquid crystal thermoset
;
thermoset
;
epoxy
;
thermotropic
;
networks
;
nematic
;
smectic
;
Chemistry
;
Polymer and Materials Science
Source:
Wiley InterScience Backfile Collection 1832-2000
Topics:
Chemistry and Pharmacology
Notes:
Four new epoxy monomers have been synthesized and characterized as part of a program to prepare novel liquid crystal thermoset (LCT) materials. Three of the new epoxy monomers contained a biphenyl mesogen and were not liquid crystalline (LC). The remaining epoxy monomer, which contained a 1,4-dibenzoyloxybenzene mesogen, was synthesized in an overall yield of 30% and displayed a broad (83°C) nematic liquid crystalline phase. The new liquid crystalline epoxy monomer was cured at 120°C and postcured at 175°C with a stoichiometric amount of 1,4-phenylenediamine. The thermal transitions of the resulting LCT were studied by differential scanning calorimetry (DSC), polarized light optical microscopy (POM), thermomechanical analysis (TMA), and wide angle x-ray diffraction (WAXD) as a function of cure time and temperature. A process characterization diagram was constructed which shows that LCTs based on this new LC monomer can be processed in the liquid crystalline phase over a broad range of times and temperatures. Qualitative agreement with previous epoxy LCT results was found, as LCT's with smectic phases and without clearing temperatures were observed at long cure times (high crosslink densities), whereas nematic phases with clearing temperatures predominated in networks at short cure times (low crosslink densities). © 1993 John Wiley & Sons, Inc.
Additional Material:
9 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/pola.1993.080310908
Permalink