    Description: Troilite formation via the reaction Fe(s) + H2S(g) + H2(g) is the major mechanism for S retention in grains in the solar nebula. Thermodynamic calculations predict that troilite condenses from a solar composition gas. We present experimental results on the kinetics and growth of troilite crystals on Fe metal at temperature (450-650 C) and composition (50-1000 ppm H2S in H2) conditions similar to those in the solar nebula. The fraction of Fe reacted (based on gravimetric data) is plotted at 450, 505, 575, and 650 C. The thickness change of unreacted iron (measured by optical microscopy) is plotted at 575 and 650 C vs. time. the weight change per unit area varies as the square root of time at the lower temperatures and varies linearly with time at the highest temperature. The growth behavior along the lower isotherms is due to diffusion. This behavior suggests sulfide diffusion to the metal-sulfide interface and suggests Fe(2+) diffusion to the sulfide-gas interface. The reaction along the highest isotherm appears to be interface controlled. The formation of troilite crystals is a rapid process forming measurable layers in a few hours. The crystalgrowth is complicated. Initially there are intergrowths of troilite into the pure Fe metal. As the reaction progresses two distinct layers of troilite crystals form. One is in contact with the Fe metal and consists of small randomly oriented crystals with pore space between them. The outermost layer contains large crystals that are all oriented in the same direction. The intergrowth layer is much smaller at 650 C than at 575 C. This suggest that FeS nucleation is inhibited at the higher temperature, accounting for the initially slower reaction rate. Once nucleated, the reaction kinetics are apparently controlled by the growth of the crystals at the interface.
    Keywords: LUNAR AND PLANETARY EXPLORATION
    Type: Meteoritics (ISSN 0026-1114); 29; 4; p. 490
    Format: text
    Location Call Number Expected Availability
    BibTip Others were also interested in ...
Close ⊗
This website uses cookies and the analysis tool Matomo. More information can be found here...