    Description: Statically oxidized Inconel 617 and MA 956 superalloys were prepared with vapor deposited aluminosilicate layers and exposed to temperatures which simulated reentry conditions. The aluminosilicate layers were 1-2 microns thick. The trials consisted of exposures to 1500-2300 F heat while surface temperatures were monitored with pyrometers. Analyses were then performed of the catalytic activity, oxidation phenomena, and radiative properties after thermal cycling the specimens for 8 hr. Both alloys were found to be catalytic to the recombination processes of dissociated species in the reentry environment. The coatings reduced the catalytic activity by 40 percent for both alloys but did not change the emittance. An enhanced Cr depletion zone was detected in the Inconel samples, implying that the coating did not prevent diffusion loss of Cr. The coated MA 956, on the other hand, gained weight over the course of the trials.
    Keywords: INORGANIC AND PHYSICAL CHEMISTRY
    Type: AIAA PAPER 85-0403
    Format: text
    Location Call Number Expected Availability
    BibTip Others were also interested in ...
Close ⊗
This website uses cookies and the analysis tool Matomo. More information can be found here...