Description:
An acousto-ultrasonic nondestructive testing method used to monitor damage during static and fatigue loading of thin graphite epoxy laminates is described. The experimental procedure, the signal analysis by the Fast Fourier Transform (FFT) algorithm, and the results of this analysis are discussed. Quasi-static tension tests showed a sharp decrease in the quantitative parameters when transverse cracks developed in the 90 degrees plies of a (0, 90/2/)s laminate. When internal micro-delaminations unite to form macro-delaminations, a sharp decrease in the parameters is also observed. The parameters are found to correlate well with other indications of damage development such as stiffness and degradation. The root mean square value of the moment is found to be more sensitive to damage than stiffness. Various signals and spectrums of graphite epoxy systems are presented.
Keywords:
COMPOSITE MATERIALS