    Electronic Resource
    Electronic Resource
    Copenhagen : International Union of Crystallography (IUCr)
    Applied crystallography online 23 (1990), S. 266-276 
    ISSN: 1600-5767
    Source: Crystallography Journals Online : IUCR Backfile Archive 1948-2001
    Topics: Geosciences , Physics
    Notes: The decomposition process of the supersaturated solid solution Cu–15wt%Ni–8wt%Sn prepared by powder metallurgy has been studied by anomalous small-angle scattering of X-rays. The ageing has been followed at 623 K. The analysis of the small-angle scattering intensities shows that the spinodal decomposition model accounts neither for the measured contrast of the electronic densities nor for the anomalous effects observed near the absorption edges of the elements contained in the sample. The measured intensity variation is large and of opposite sign when the Cu and Ni edges are approached from the lower energy side: a decrease of 30% for an energy variation from 292 to 8 eV below the Ni K-absorption edge and a sharp increase of 140% from 300 to 7 eV below the Cu K edge. A comparison with previous studies on the same system indicates that the decomposition process investigated in our samples corresponds more to the nucleation and growth regime than to the spinodal one. We found that the assumption of (Cu0.52Ni0.48)3Sn precipitates having D022 structure is in agreement with our experimental results.
    Type of Medium: Electronic Resource
    Location Call Number Expected Availability
    BibTip Others were also interested in ...
Close ⊗
This website uses cookies and the analysis tool Matomo. More information can be found here...