Summary The crystallization behaviour of polyethylene, of the amylose-alcohol-complexes and of the amylose-iodinecomplex is compared. Polyethylene and the amylose-alcohol-complexes are similar; flat single crystals or crystallites are formed. The temperature dependence of the foldlengths and of the crystal diameters is lower than expected by the kinetic theory ofLauritzen andHoffman. It is proposed, that these deviations are due to the temperature dependence of chain stiffness of the coiled molecules in solution. With the amylose-iodine-complex only fibrils are formed. One can get single rodlike molecules with a uniform diameter of 40 Å.
Notes:
Zusammenfassung Es wird das Kristallisationsverhalten des Polyäthylens, der Amylose-Alkohol-Komplexe und des Amylose-Jod-Komplexes verglichen. Polyäthylen und die Amylose-Alkohol-Komplexe verhalten sich ähnlich; es bilden sich flächige Einkristalle oder Kristallite. Die Temperaturabhängigkeit der Faltlängen und Kristallgrößen ist bei Polyäthylen und besonders bei den Amylose-Alkohol-Komplexen geringer, als nach der Theorie vonLauritzen undHoffman zu erwarten ist. Es wird vorgeschlagen, diese Abweichungen auf die Temperaturabhängigkeit der Kettensteifheit in den Molekülknäueln zurückzuführen. Bei dem Amylose-Jod-Komplex entstehen ausschließlich Fibrillen. Es konnten einzelne Moleküle in der Form von Stäbchen mit einem einheitlichen Durchmesser von ca. 40 Å im Elektronenmikroskop abgebildet werden.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF01500161