Description / Table of Contents:
The results obtained in investigating the long chain branching of high pressure polyethylene (LDPE) and emulsion polybutadiene (PB-E) are provided. Besides 13C NMR data measured in the low and high field region (with hydrated PB-E) comparative values of molecule contraction in solution are considered. The change of the molecular weight distribution and the relationships between molecular weight and intrinsic viscosity in dependence on conversion in the emulsion polymerization of butadiene was investigated. The data required for determining the contraction factor were obtained by combining gel permeation chromatography and solution viscosity measurements. The differences of the results are discussed with respect to their causes.
Notes:
Es wird über Ergebnisse von Langkettenverzweigungsanalysen am Hochdruckpolyethylen (PE-LD) und Emulsionspolybutadien (PB-E) berichtet. Die Ergebnisse aus der 13C-NMR-Spektroskopie im niederen und hohen Feldbereich (am hydrierten PB-E) werden mit Informationen aus den Untersuchungen zur Molekülkontraktion in Lösung verglichen. Die änderungen der Molmassenverteilung sowie die Zusammenhänge zwischen Molmasse und Grenzviskosität als Funktion des Umsatzes bei der Emulsionspolymerisation des Butadiens wurden untersucht. Die Daten zur Bestimmung des Kontraktionsfaktors g′GPC wurden aus der Kombination von Gelpermeationschromatographie und Viskositätsmessungen erhalten. Die Ursachen für die unterschiedlichen Resultate werden diskutiert.
Additional Material:
7 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/actp.1983.010340608