Crystal Structure and Electrical Conductivity of Ag3YCl6The reaction of YCl3 with an AgCl single crystal in a sandwich diffusion couple (365°C, 140 h) leads to a product layer of single crystalline Ag3YCl6. Single crystals of low-temperature Ag3YCl6-I transform to high-temperature Ag3YCl6-II at 350°C. Ag3YCl6-I (a = 686.69 pm, c = 1830.5 pm, trigonal, R3, Z = 3) is isostructural with Na3GdCl6-I. The compound shows structural disorder with two Ag+-ions occupying statistically half of four octahedral interstices. The specific electrical conductivity of Ag3YCl6 was investigated from room temperature up to the melting point (T = 413°C). The transition from low to high-temperature Ag3YCl6 is accompanied by a sharp increase of the conductivity.
Notes:
Polykristallines YCl3 reagiert mit einem Einkristall von AgCl in Sandwich-Anordnung (365°C, 140 h) an der Kontaktfläche zu einer Produktschicht aus vorwiegend einkristallinem Ag3YCl6. Die daraus isolierten Einkristalle der Tieftemperaturform (Ag3YCl6-I) wandeln sich bei 350°C in eine Hochtemperaturform (Ag3YCl6-II) um. Die Kristallstruktur von Ag3YCl6 I (a = 686,69 pm, c = 1 830,5 pm, trigonal, R3, Z = 3) entspricht der des Na3GdCl6-I. Es liegt eine strukturelle Fehlordnung vor, wobei zwei Ag+-Ionen vier Oktaederlücken statistisch jeweils zur Hälfte besetzen. Die spezifische elektrische Leitfähigkeit von Ag3YCl6 wurde von Raumtemperatur bis oberhalb des Schmelzpunktes (T = 413°C) untersucht. Die Umwandlung der Tiefin die Hochtemperaturform ist von einem sprunghaften Anstieg der Leitfähigkeit begleitet.
Additional Material:
4 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19905820118