Studies on Nickel Oxide Mixed Catalysts. I. Structural Properties of NiO/SiO2 CatalystsStructural properties of NiO/SiO2 catalysts prepared by precipitation-deposition and impregnation have been investigated. A nickel-layer-silicate like structure is formed only in the precipitated catalysts showed infrared spectroscopic measurements. After thermal treatment at 723 K by means of magnetic measurements and reflectance spectroscopy besides Ni2+ ions in octahedral environment tetrahedral coordinated Ni2+ions were found. The part of tetrahedral coordinated Ni2+ ions is independent of the NiO-content up to 40 mole % NiO. Nickel oxide is formed above a content of 40 mole %.In the case of the impregnated catalysts nickel oxide cluster are formed on the surface after annealing at 723 K.
Notes:
Es wurden die strukturellen Eigenschaften von durch Fällung und Tränkung hergestellten NiO/SiO2-Katalysatoren untersucht. Infraspektroskopische Messungen zeigten, daß sich bei den durch Fällung hergestellten Katalysatoren wenig strukturierte Nickelschichtsilikate bilden. Nach thermischer Behandlung bei 723 K wurden durch magnetische und UV-VIS-reflexionsspektroskopische Untersuchungen neben Ni2+-Ionen in oktaedrischer Sauertoffkoordination auch tetraedrisch koordinierte Ni2+-Ionen nachgewiesen. Der Anteil an tetraedrisch koordinierten Ni2+-Ionen ist bis 40 Mol-% NiO nicht vom NiO-Gehalt abhängig.Im Unterschied dazu sind bei den durch Tränkung hergestellten Katalysatoren die Wechsel-wirkungen zwischen den Komponenten gering. Auf der Oberfläche dieser Katalysatoren bilden sich nach Temperung Nickeloxidcluster.
Additional Material:
3 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19804670106