Investigations on Metal Catalysts. XVIII. Phase Shaping, Dispersity, and Surface Composition of Ni—Cu—Re CatalystsCatalysts of the system Ni—Cu—Re reduced at 500°C consist of the following phases: only one f.c.c. phase in Ni—Cu samples, in Ni—Cu—Re samples with ≥10 at.-% Re there is an additional h.c.p. phase (pure Re). The greatest solubility in regard to rhenium (but never 〉 10 at.-%) was observed in the case of catalysts with a Ni:Cu ratio of 1:1. Ni—Cu—Re samples show considerably higher surface areas than the nickel sample. The catalyst Ni 45 Cu 45 Re 10 exhibits the maximum surface area. The surface layer of the crystallites is enriched with copper.
Notes:
Bei einer Reduktionstemperatur von 500°C hergestellte Katalysatoren des Systems Ni—Cu—Re weisen folgende Phasen auf: Ni—Cu-Proben sind durch nur eine kubischflächenzentriert kristallisierte Phase gekennzeichnet; in Proben mit Gehalten ≥10 At.-% Re liegt freies (hexagonal kristallisiertes) Re vor. Die größte Löslichkeit für Rhenium, die 10 At.-% nicht übersteigt, wurde bei Proben mit einem Ni: Cu-Verhältnis von 1:1 festgestellt. Ni—Cu—Re-Katalysatoren sind erheblich oberflächenreicher als der entsprechende Ni-Katalysator. Die maximale Oberflächengröße wird in der Probe Ni 45 Cu 45 Re 10 erreicht. In der Oberfläche der Ni—Cu—Re-Katalysatoren ist Kupfer angereichert.
Additional Material:
4 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19774360128