Beschreibung / Inhaltsverzeichnis:
A series of ferric oxides with additional CaO in the range of 0 to 50 mole per cent were characterized after heating at 600°C by x-ray investigations, estimation of the specific surfaces, and catalytically by means of N2O decomposition and dehydrogenation of isopropyl alcohol.In the range of lower additions of CaO, especially 0.3 mole per cent, maximal catalytical values are found for both test reactions, accompanied by a maximal lattice extension of α-Fe2O3 and Fe3O4, respectively.The doping effect is interpreted by taking into consideration the reaction mechanisms and the variations of semiconductor properties of the oxides owing to limited Ca2+ insertion.
Notizen:
Eine Reihe von Eisen(III)-oxiden mit CaO-Zusätzen von 0-50 Mol-% wird nach der Temperung bei 600°C röntgenographisch, durch Bestimmung der spezifischen Oberflächen sowie katalytisch an Hand der N2O-Zersetzung und der Isopropanoldehydrierung charakterisiert.Im Bereich geringer CaO-Zusätze, insbesondere bei etwa 0,3 Mol-%, ergeben sich übereinstimmend für beide Testreaktionen katalytische Maximalwerte, die von einer maximalen Gitterdehnung des α-Fe2O3 bzw. Fe3O4 begleitet werden. Der Dotierungseffekt wird unter Beachtung des Mechanismus der beiden katalytischen Reaktionen und der Zunahme des p-Leitercharakters (bzw. Veminderung des n-Leitercharakters) der Eisenoxide infolge Ca2+-Einbau gedeutet.
Zusätzliches Material:
3 Tab.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/zaac.19693640303