In this study, we conducted a quantitative evaluation of dislocation density by scanning electron microscopy electron channeling contrast imaging for α grains of a Ti-6Al-4V alloy deformed at room temperature. The depth of visibility of dislocations is experimentally measured as 140-160 nm by a serial sectioning observation. This result is compared to the theoretical value and applied to evaluate dislocation density. These factors confirm that the theoretically calculated value of the depth of visibility, at five to six times the extinction distance, is valid for the HCP-Ti alloy.