The local structure of cerium in two systematic compositional series of glasses, nominally CeP 3 O 9 –AlP 3 O 9 and CeP 3 O 9 –SiP 2 O 7 , was interrogated using X-ray photoelectron spectroscopy (XPS) and X-ray absorption fine structure (XAFS) spectroscopy. XPS revealed that, for glasses melted in air, ≥95% of cerium ions are Ce 3+ . This was independently confirmed using X-ray absorption near edge spectroscopy (XANES). Ce K-edge extended X-ray absorption fine structure (EXAFS) has been used to determine the local structure of Ce 3+ . Near the metaphosphate composition, cerium was found to have an average cerium coordination number of ~7.0 and an average cerium-oxygen bond length of 2.41 Å. The average cerium coordination number and average cerium-oxygen bond distance were found to increase with decreasing cerium concentration in both compositional series. Rare-earth clustering is suggested based on numerical calculations for glasses containing ≥14 and ≥15 mol% Ce 2 O 3 for the aluminophosphate and silicophosphate series, respectively.
Print ISSN:
0002-7820
Electronic ISSN:
1551-2916
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics