In n-type Czochralski silicon (Cz-Si) wafer, swirl shaped regions with low lifetime (known as striations) can cause degradation up to 1% absolute or even more in homojunction industrial solar cells. Nevertheless, the nature of the defects responsible for the occurrence of these striations is still unclear. In this work, n-type Cz-Si solar cell precursors cut from industrial size ingots with different feedstock quality and oxygen content were analyzed by microwave photo-conductance decay and photoluminescence in order to investigate the nature of such defects. The results demonstrate that the defects responsible for the occurrence of striations are oxide nanoprecipitates formed during the high temperature steps for the solar cell realization, due to the presence of grown-in oxygen nuclei.