The cube texture formation during primary recrystallization was analysed in plane strain deformed samples of a commercial AA1050 alloy and an Al-1%wt.Mn model alloy single crystal of the Goss{110} orientation. The textures were measured with the use of X-ray diffraction and scanning electron microscopy equipped with an electron backscattered diffraction facility. After recrystallization of the Al-1%wt.Mn single crystal, the texture of the recrystallized grains was dominated by four variants of the S{123} orientation. The cube grains were only sporadically detected by the SEM/EBSD system. Nevertheless, an increased density of poles corresponding to the cube orientation was observed. The latter was connected with the superposition of four variants of the S{123} orientation. This indicates that the cube texture after the recrystallization was a ?compromise texture?. In the case of the recrystallized AA1050 alloy, the strong cube texture r...
Print ISSN:
1757-8981
Electronic ISSN:
1757-899X
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics