Description: The goal of this program was to evaluate the low cycle fatigue behavior of an SCS-6/Ti-6Al-4V sub-component under bi-axial loading conditions at 316 C(600 F). A simulated bladed TMC disk was designed having thirty four blades representing the number that would be used in Allied Signal's JTAGG II impeller. The outer diameter of the bladed ring was 254 mm (10.0 inch) and the inner diameter 114.3 mm (4.50 inch). The outer and inner diameter of the composite zone was 177.8 mm (7.00 inch) and 127.O mm(5.00 inch) respectively. Stress analysis showed that the fatigue life of the bladed composite ring would be about 12000 cycles for the test conditions applied. A modal analysis was conducted which showed that the blades would have sufficient life margin from dynamic excitation. The arbor design was the same as that employed in the spin-to burst test of NAS3-27027. A systematic stress analysis of each part making up the arbor was undertaken to assure the design would meet the low cycle fatigue requirements of the program. The Textron Systems grooved foil-fiber process was chosen to make the SCS-6/Ti-6Al-4V core ring based on the success they had in contract NAS3-27027. Fiber buckling, however, was observed at several locations in the first ring made which rendered it unsuitable for spin testing. The fiber buckling was attributed to cracking of the graphite tooling during the consolidation process. On this basis a second ring was made but it too contained fiber buckling defects. Analysis by Textron indicated that the fiber buckling was most likely due to poor placement of the SCS-6 fiber in the etched grooves of the Ti-6Al-4V foil. This was also a contributor to the defects in the first ring. Since there was little indication of control in the process to manufacture a quality ring a third attempt at making a ring was not undertaken.