Microstructural changes occurring during sliding wear of self-mated Al2O3 SiC whisker-reinforced composites were studied using optical, scanning electron microscopy and transmission electron microscopy. Pin-on-disc specimens were slid in air at 2.7 m/s sliding velocity under a 26.5 N load for 1 h. Wear tests were conducted at 23, 600, 800 and 1200 C. Mild wear with a wear factor of 2.4 x 10 exp -7 - 1.5 x 10 exp -6 cu mm /N per m was experienced at all test temperatures. The composite showed evidence of wear by fatigue mechanisms at 800 C and below. Tribochemical reaction (SiC oxidation and reaction of SiO2 and Al2O3) leads to intergranular failure at 1200 C. Distinct microstructural differences existing at each test temperature are reported.
Schlagwort(e):
COMPOSITE MATERIALS
Materialart:
Journal of Materials Science (ISSN 0022-2461); 28; 5; p. 1147-1154.