This paper examines the use of a thin layer of Ultra High Molecular Weight Polyethylene (UHMWPE) on the outer surface of carbon/epoxy composite materials as a method of improving impact resistance and damage tolerance through hybridization. Flat 16-ply laminates as well as honeycomb sandwich structures with eight-ply facesheets were tested in this study. Instrumented drop-weight impact testing was used to inflict damage upon the specimens. Evaluation of damage resistance included instrumented impact data, visual examination, C-scanning and compression after impact (CAI) testing. The results show that only one lamina of UHMWPE did not improve the damage tolerance (strength retention) of the 16-ply flat laminate specimens or the honeycomb sandwich beams, however, a modest gain in impact resistance (detectable damage) was found for the honeycomb sandwich specimens that contained an outer layer of UHMWPE.
Keywords:
COMPOSITE MATERIALS
Type:
Composites Engineering (ISSN 0961-9526); 3; 5; p. 383-391, 393, 394
Format:
text