Description:
The source of the asymmetry in the dislocation morphology exhibited in the epitaxial growth of compound semiconductors on (100) was investigated. A thickness wedge of p- and n-type GaAs(0.95)P(0.05) was grown on GaAs by metalorganic chemical vapor deposition, and the effect of misorientation on the resolved shear stress for each slip system was calculated and eliminated as the source of the asymmetry. Another potential source of asymmetry, the thickness gradient, was also eliminated. Results show that the substrate misorientation and the thickness gradient do not significantly contribute to the asymmetry and that the dominant contributor to the asymmetry of misfit dislocations in the (001) epitaxial interface can be attributed to the differences in the Peierls barriers between the two types of dilocations in GaAsP/GaAs.