This paper describes the synthesis of maleimide terminated poly(ether ketones) using the solution imidization process described by Summers et al. (1987). Amorphous poly(arylene ether ketones), as well as poly(arylene ether sulfones, of controlled end group functionalities and molecular weights were synthesized by nucleophilic step polymerization of bisphehol-A phenolates with activated halides, such as 4,4'-difluorobenzophenone, and 'monofunctional' end cappers such as m-aminophenol. The thermal properties of the system included glass transition temperature (Tg) values of 160-170 C, with modulus above Tg proportional to cross-link density, which in turn was reciprocally related to oligomer molecular weight. The measurements of the fracture toughness values showed the materials to be very ductile, with the toughness increasing with oligomer molecular weight.