Publication Date:
2006-02-14
Description:
Fracture behavior of tensile specimens containing through-the-thickness flaws and part-through semi-elliptic surface flaws was investigated. The material was T300/5208 graphite/epoxy, with a stacking sequence 0/+ or - 45/90 sub ns. Laminate thicknesses ranged from 8 to 120 plies. Fracture toughness for specimens with through-the-thickness flaws was a function of laminate thickness. Fracture toughness was also independent of crack size. Fracture toughness for the thick laminates was also independent of specimen geometry (center-cracked tension specimen, compact tension specimen, and three-point bend specimen). Using the asymptotic value of facture toughness and linear elastic isotropic fracture mechanics, the notched strength of tensile specimens with semi-elliptic surface flaws was predicted. The strength ratio is a function of the flaw depth (a/t) and flaw aspect (a/c) ratios. Comparisons between predicted and experimental strengths are good for large values of a/t. The notched strength of filament wound graphite/epoxy tensile specimens with part-through surface flaws was also predicted.
Keywords:
COMPOSITE MATERIALS
Type:
Proceedings of the 2nd Annual Review of the Center for Composite Materials and Structures; 11 p
Format:
text