Publikationsdatum:
2019-06-27
Beschreibung:
Splat cooled Al-Si solid solutions with 1 to 11 at.% Si were prepared and their precipitation kinetics were studied by transmission electron microscopy. The time required for appearance of particles visible at a magnification of 35,000 times was determined at temperatures between 248 K and 573 K. The resulting Arrhenius plots yielded activation energies ranging from 55 to 40 plus or minus 2kJ/mol over the composition range. Precipitate densities were higher and denuded zones of 100 to 150 nm were narrower than in comparable solid quenched samples. The activation energies are explained in terms of excess point defect concentrations.
Schlagwort(e):
METALLIC MATERIALS
Materialart:
Metallurgical Transactions A - Physical Metallurgy and Materials Science; 6A; Dec. 197