ISSN:
1573-4889
Keywords:
chloridation
;
oxidation
;
Fe-Cr alloys
;
Ni-Cr alloys
Source:
Springer Online Journal Archives 1860-2000
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
Abstract The chloridation-oxidation behavior of Fe-Cr (0–25 wt. %Cr) and Ni-Cr (0–20 wt.%Cr) alloys was studied at 800°C in three different H2-HCl-H2O(ν) environments. In a low-HCI and low-H2O(ν) environment, where Cr2O3 is thermodynamically stable, the corrosion resistance of the Fe-Cr alloys increased with increasing Cr content in the alloys. In a high-HCl and high-H2O(ν) environment, where FeCr2O4 is stable and CrCl2 is metastable, the corrosion resistance of the Fe-Cr alloys depended similarly on the Cr content. Low-Cr-Fe-Cr alloys exhibited large weight losses, while Fe-Cr alloys with higher than 19 wt. %Cr showed good corrosion resistance. In an environment of high-HCl in the absence of H2O(ν), the evaporative corrosion rate was fast and limited by gas phase diffusion, and independent of the Cr content in the Fe-Cr alloys. Ni and Ni-Cr alloys generally showed good corrosion resistance in the environments of high H2O(ν) because of the low NiCl2 vapor pressure and formation of a protective Cr2O3 scale. However, in the environment of high HCl in the absence of H2O(ν), selective formation and evaporation of CrCl2 occur, which results in Cr depletion and networks of voids for even a high-Cr Ni-Cr alloy.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF02153464