Polycarbonates from 4,4′-Dioxy-diphenyl-2,2-propan, 4,4′-Dioxy-diphenylmethan, and 4,4′-Dioxy-diphenyl-sulfid crystallize from the melt with spherulitic structure and athermal nucleation. Depending on crystallization conditions different morphological textures were observed.The rate of spherulite growth, measured by means of polarisation microscope, depends on the chemical structure of the polycarbonate. The crystallization of polycarbonates from 4,4′-Dioxy-diphenyl-2,2-propan is hindered by the spacefilling isopropyl-group. On the other hand, polycarbonates from 4,4′-Dioxy-diphenyl-methan and 4,4′-Dioxy-diphenyl-sulfid have a relatively high tendency to crystallisation.
Notes:
Polycarbonate auf der Basis 4,4′-Dioxy-diphenyl-2,2-propan, 4,4′-Dioxy-diphenylmethan und 4,4′-Dioxy-diphenyl-sulfid kristallisieren mit athermischer Keimbildung aus der Schmelze sphärolithisch. Es wurden verschiedene morphologische Strukturen beobachtet.Die lichtmikroskopische Bestimmung der Sphärolith-Wachstumsgeschwindigkeit läßt eine unterschiedliche Kristallisationsneigung der betrachteten aromatischen Polycarbonate erkennen. Danach zeigt das Polycarbonat auf Basis 4,4′-Dioxy-diphenyl-2,2-propan ein stark gehemmtes und verzögertes Kristallisationsverhalten, während die Polycarbonate auf Basis 4,4′-Dioxy-diphenyl-methan und 4,4′-Dioxy-diphenylsulfid als relative kristallisationsfreudig zu bezeichnen sind. Als Ursache für das unterschiedliche Kristallisationsverhalten wird der verschiedenartige molekular Aufbau diskutiert.
Additional Material:
1 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/macp.1964.020750110