The effects of atomic oxygen on several classes of polymers were investigated. Particular attention was directed to the determination of erosion or mass loss mechanisms in relation to the physical and chemical structures of polymers. Nineteen polymeric materials were exposed to a thermal atomic oxygen environment at fluxes of 1022 atoms/m2-sec. Bulk material temperatures were maintained at 10, 45, and 75°C During exposure. Mass loss rate, which was characteristic of the type of polymer, was proportional to the exposure area and was linear in time for most polymers except for Mylar, which produced a shielding high temperature ash. The mass loss rate for the atomic oxygen degradation of polymers was related to the bond strength of the polymer structure and to the shielding effect of pendant structures. This degradation process was strongly dependent on polymer temperature. Activation energies ranged from 1 to 48 KJ / mole and were found to be related to gaseous diffusion in polymers. Frequency factors were proportional to activation energies. Activation energies were found to increase with increased mol wt and crosslinking. An equation was developed relating exposure area, atomic oxygen flux, frequency factor, and activation energy to the rate of polymer mass loss. © 1993 John Wiley & Sons, Inc.
Additional Material:
18 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/app.1993.070480804