Influence of Oxygen Traces on the Properties of Tungsten Heavy MetalsInvestigation carried out with differently sintered W heavy metals showed that careful pre-reduction before liquid phase sintering is essential for obtaining satisfactory mechanical properties; otherwise oxide layers at the phase boundaries deteriorate the interface strength and thus cause premature fracture. Understandably, the water vapour content of the furnace atmosphere is of considerable importance. Appropriate sintering anticipated, even severely oxidized green compacts result in highly ductile heavy metals. Addition of scavengers, e.g. Cr or V, instead of the pre-reduction improves the interface strength, the mechanical properties however remain unsatisfactory.
Notes:
Untersuchungen an nach verschiedenen Zyklen gesinterten Schwermetallen zeigten, daß sorgfältige Reduktion vor dem Flüssigphasensintern notwendig ist, um die beträchtlichen Ausgangsmengen an Sauerstoff zu entfernen; andernfalls werden aufgrund der durch Oxidbelegung verschlechterten Haftfestigkeit zwischen W-Körnern und Binderphase nur sehr schlechte mechanische Eigenschaften erhalten. Der Wassergehalt der Ofenatmosphäre spielt naturgemäß eine bedeutende Rolle; bei richtiger Führung der Sinterung werden auch von stark oxidierten Grünlingen ausgezeichnete Schwermetalle erhalten. Zusatz von Scavengern, wie Cr oder V, anstatt der Vorreduktion verbessert zwar die Haftung der Phasen, die Eigenschaften bleiben aber unbefriedigend.
Additional Material:
10 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/mawe.19840150306