Description / Table of Contents:
Crystal Structure of the Low Temperature Modification of RuTe2Black shining, platelet like single crystals of α-RuTe2 were obtained by chemical transport reaction with Cl2/AlCl3 (crystal dimensions up to 1 mm). The crystal structure of this low temperature modification of α-RuTe2 hitherto only known from powder measurements, was redetermined at room temperature by single crystal X-ray diffraction on a four-circle diffractometer. α-RuTe2 crystallizes in the marcasit structure typ in the orthorhombic spacegroup Pnnm (No. 58) with the lattice constants a = 528.12(13), b = 639.43(19), c = 400.85(13) pm.
Notes:
Durch chemischen Transport mit dem Transportmittel Cl2/AlCl3 konnten schwarzglänzende, plattenartige Einkristalle von α-RuTe2 erhalten werden (Kantenlänge bis zu 1 mm). Die Kristallstruktur dieser bisher nur aus Pulverdaten bekannten Tieftemperaturmodifikation von RuTe2 wurde röntgenographisch an einem Einkristall auf einem Vierkreisdiffraktometer bei Raumtemperatur neu bestimmt. α-RuTe2 kristallisiert im Markasit-Strukturtyp in der orthorhombischen Raumgruppe Pnnm (Nr. 58) mit den Gitterkonstanten a = 528,12(13), b = 639,43(19), c = 400,85(13) pm.
Additional Material:
1 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19976231029