ALBERT

Notizen: Stress intensity factors are determined for internally and externally cracked, pressurized thick cylinders with partial autofrettage (less than 100% overstrain). The solutions are based on a superposition of existing solutions which does not involve any loss of accuracy. Implications of the stress intensity factor results for the safe-life design of pressure vessels subjected to fatigue are discussed.

Notizen: Fatigue crack propagation tests were conducted under conditions of equibiaxial, uniaxial and shear loading by using a cruciform specimen in a servo hydraulic testing machine. The effect of non-singular stress cycling on the fatigue crack propagation rate was examined based on the observation of crack opening behavior. The crack propagation rate was significantly influenced by the non-singular stress parallel to the crack when it was correlated to the stress intensity range. The crack closure behavior was greatly affected by the non-singular stress. The crack propagation rate was uniquely correlated to the effective range of the stress intensity factor except for the case of completely reversed shear loading where significant plasticity was detected. The crack opening displacement range was concluded to be a parameter controlling the crack propagation rate for all the stress conditions examined in the present experiments. Some discussion is made on the effect of material anisotropy on fatigue crack propagation in a biaxial stress field.

Notizen: The paper presents a comprehensive review, supplemented by original data, of the engineering fatigue behaviour of copper. Variations in manufacturing route and softening treatments are shown to have little effect on the fatigue of annealed copper but the high cycle fatigue strength is increased by cold work. The high strain fatigue behaviour is defined in terms of the plastic strain range and the cyclic stress-strain characteristics are documented. Fatigue behaviour in bending and torsion is defined by data and related to that in tension by simple design rules.Notches are found to reduce the laboratory measured fatigue strength of copper by ∼ 30% and the effect of surface finish, surface distortion and surface residual stress is defined in the literature. Fatigue crack growth is defined in terms of stress intensity factor range ΔK by an upperbound law and, together with the conditions for non-growth (ΔK0), shown to relate to the equivalent conditions for steels via the ratio of the respective elastic moduli.The effect of environment on the fatigue of copper has received scant attention in the literature, such results as exist suggesting little if any reduction in strength to be brought about by gaseous or aqueous environments. The most dramatic change is the improvement of about an order of magnitude which results when tests in vacuum are compared with equivalent tests in air. Results of fatigue tests on copper in ammoniacal environments are conspicuously absent from the literature.As the test temperature is reduced below room temperature there is a predictable increase in high cycle fatigue strength, a reduction in fatigue strength occurring above room temperature. High strain fatigue test results presented in terms of plastic strain range appear insensitive to temperature although at very low strain rates and high temperatures a reduction in fatigue strength occurs. A linear life fraction cumulative damage creep-fatigue law appears sometimes to be non-conservative but much more testing is needed to evaluate fatigue damage summation laws generally for copper.Numerical data are given in support of all the aspects of the engineering fatigue behaviour reviewed in the paper.

Notizen: The birth and growth of short cracks is analysed from an elastic-plastic fracture mechanics viewpoint. Low to high cumulative damage tests from the low stress to high strain regime indicate that there is no crack initiation period in the metallurgical sense and that cracks grow from the first cycle, but at a slow rate. The initiation phase terminates when one crack starts to dominate and accelerates to failure, its initial size being given by 〈displayedItem type="mathematics" xml:id="mu1" numbered="no"〉〈mediaResource alt="image" href="urn:x-wiley:8756758X:FFE263:FFE_263_mu1"/〉 for the medium carbon steel tested here, of grain size 56 μm.

Notizen: Fractographic analyses have been used to explain the cyclic crack growth behaviour of A533-B, Ducol W30, a C-Mn steel and type 304 stainless steel in simulated light water reactor environments at ambient temperature. Fractographic observations have offered an explanation for anomalous crack growth behaviour and have also indicated where micro structural or environmental variables dominate in producing certain fracture modes and crack growth rates. An understanding of the operative corrosion fatigue mechanisms has been formulated through these fractographic analyses. Environmental crack growth in the ferritic steels has been described by a model involving both anodic dissolution and hydrogen embrittlement. Conditions where only one of these mechanisms would dominate have been identified and limits to their effect postulated. A crystallographic mode of failure observed in the austenitic type 304 stainless steel has also been explained by a selective dissolution process.

Notizen: Abstract —Low-cycle fatigue properties were investigated on four carbon steels and five low alloy steels specified in JIS (Japanese Industrial Standard) for machine structural use, which are the most commonly used in Japan. Several different heats from each of several representative manufacturers were sampled so as to represent the average fatigue characteristics of current materials. The cyclic deformation behaviour of material was denned by comparing the monotonie yield stress on the extrapolated tensile work hardening curve with the cyclic yield stress in the cyclic stress-strain curve determined by incremental step test. The normalized ferrite-pearlitic steels cyclically hardened, while the quench-tempered martensitic were cyclically stable or softened. The S–N relations derived from the strain-controlled low-cycle tests were compared with the results obtained by load-controlled high-cycle tests. The extrapolated S–N curves based on the cyclic stress-strain curve predicted the fatigue strength in the high-cycle range to be stronger for cyclic-hardening steels, but weaker for cyclic-softening steels. The predicted S–N curves for stable steels coincided with the high cycle test data. The fatigue limit had a proportional relationship with cyclic yield stress, slightly depending on the cyclic deformation behaviour. On the other hand, the cyclic yield stress was found to exhibit a very good linear correlation with the monotonie tensile strength, independent of cyclic deformation behaviour. This explains the empirical law that the fatigue limit is approximately proportional to the tensile strength.

Notizen: Recently a controversy has developed over whether crystallographic crack growth near threshold in Ni-base superalloys occurs along {111} slip planes or {100} planes at room temperature. In this work on Nimonic API crack propagation is shown to occur on both {100} and {111} planes. The most common facet plane is {111} and this is the only orientation observed at the lowest stress intensities, but at higher stress intensities occasional {100} facets are also produced. This behaviour is compared with similar results in aluminium alloys.

Notizen: A crack nucleation model is constructed based on the random slip of the dislocations within the fatal persistent slip band (PSB). From such a model, we derive the notch-peak probability function. The crack is considered to nucleate when a critical notch depth is attained. This depth is constant for applied strains corresponding to the plateau of the cyclic stress- strain curve because the stress is constant. The PSBs behave in such a way that the more concentrated their localized slip the fewer the cycles required to attain the critical notch depth. Using the experimental relation between the applied strain and the magnitude of the slip offsets (reported in Part I) in conjunction with observations of the notch distributions along the gage surface, we have obtained the relation between the applied strain and the cycles for crack nucleation. A log-log plot of this relation shows a slightly different slope from that of the Coffin-Manson life data, previously reported. However, by allowing for cycles spent in Stage II propagation, good agreement is obtained.

Notizen: The statistical nature of fatigue crack growth rate has been examined for G41400 steel exposed to different heat treatments and for different loading and environmental conditions. Techniques for determining the intrinsic value of the crack propagation rate are discussed. The intrinsic scatter due to the material has been evaluated and considered in terms of its effect on fatigue life prediction, both normal and log normal distributions of fatigue crack growth data being considered. It appears that the intrinsic material scatter in crack propagation rate is closely related to the scatter in total life.

Notizen: A d.c. potential drop formula has been established for monitoring crack growth in circular notched members subjected to torsion. Changes in crack depth of 20 μm can be detected in cracks growing up to 2 mm in depth.