Magnesium self-diffusion in orthoenstatite

Abstract

Magnesium self-diffusion coefficients were determined experimentally for diffusion parallel to each of the three crystallographic directions in natural orthoenstatite (En₈₈Fs₁₂). Experiments were conducted at 1 atm in CO-CO₂ gas mixing furnaces, which provided oxygen fugacities equivalent to the iron-wüstite buffer. Diffusion of ²⁵Mg was induced in polished samples of oriented orthoenstatite using a film of isotopically enriched ²⁵MgO as the source material. Very short (<0.15 μm) diffusional penetration profiles were measured by ion microprobe depth profiling. The diffusion coefficients determined for four temperatures (900, 850, 800, 750 °C) provide the activation energies, E _a , and frequency factors, D _o, where D = D _o exp (−E _a /RT) for Mg self-diffusion parallel to each crystallographic direction: a-axis, E _a  = 360 ± 52 kJ/mole and D _o = 1.10 × 10⁻⁴ m²/s; b-axis, E _a  = 339 ± 77 kJ/mole and D _o = 6.93 × 10⁻⁶ m²/s and c-axis, E _a  = 265 ± 66 kJ/mole and D _o = 4.34 × 10⁻⁹ m²/s. In this temperature range, any possible anisotropy of cation diffusion is very small, however the activation energy for diffusion parallel to the c-axis (001) is the lowest and the activation energies for diffusion parallel to the a-axis (100) and b-axis (010) are higher. Application of these diffusion results to the silicate phases of the Lowicz mesosiderite meteorite provides cooling rates for the silicate portion of the meteorite (4–11 °C/100 years) that are similar, although slower, to previous estimates. These silicate cooling rates are still several orders of magnitude faster than the cooling rates (0.1 °C/10⁶ years) for the metal portions.