Summary
Styrene-co-butyl methacrylate colloids were obtained by codeposition at 77 K of the monomers with several metals such as Pd, Au, Ag, Cu, Zn, Cd, Ga, In, Ge, Sn, Sb and Bi. The colloids were copolymerized with different amounts of initiator (BPO) at 65°C for 3.0 h and a wide range of viscosity average molecular weights (Mv, 104–105 g/mol) were obtained depending upon the metal used. The metal colloid concentration and stability are reported. A medium particle size of 60-244 Å comonomer colloids was found. The thermal stability and metal composition are also described. The copolymers are stable even at 380°C, Ga- poly(styrene-co-butyl methacrylate) being the most stable with 418°C. The metal content is ranging between 0.10 and 2.26% w/w for the highest MW fraction and between 0.20 and 2.41% w/w for the lowest MW fraction. Copolymers with different colors were obtained depending on the metal used.
Similar content being viewed by others
References
G.A. Ozin. Adv. Mater. 4, 612 (1992).
H.R. Allcock. Science, 255, 1106 (1992).
G. Cárdenas T., H. Carbacho H., E. Salgado C., M. Rodríguez B. Macromol. Symp., 84, 65 (1994).
G. Cárdenas T., E. Salgado C. and L.H. Tagle D., Thermochim. Acta 230, 259 (1993).
G. Cárdenas T. and E. Salgado C.. Polymer Bull., 35, 553 (1995).
G. Cárdenas T., E. Salgado C. and L.H. Tagle D. Int. J. Polymeric Mater.
G. Cárdenas T., C. Retamal C. and K.J. Klabunde. Polymer Bull., 27, 383 (1992).
G. Cárdenas T. and L.H. Tagle D. Thermochim. Acta. 200, 361 (1992).
G. Cárdenas T. and K.J. Klabunde. Bol. Soc. Chil. Quím., 33, 163 (1988).
Y. Almong, S. Reich and M. Levy, Brit. Polym. J., 14, 131 (1982).
C.M. Tseng, Y.Y. Lu, M.S. El-Aasser and J.N. Venderloff. J. Polym. Sci. Chem., 24, 2993 (1986).
G. Cárdenas T., K.J. Klabunde and E.B. Dale, Langmuir, 3, 986 (1987).
F.W. Billmeyer “Textbook of Polymer Science”, 2nd Ed. Wiley-Interscience, N. York, 290 (1962).
J. Brandrup and E.H. Immergut. “Polymer Handbook”. J. Wiley & Sons, 3rd Ed. VII (1989).
G. Cárdenas-Triviño, C. Retamal C. and K.J. Klabunde. J. Appl. Polymer Sci.: Polymer Symp., 49, 15 (1991).
G. Cárdenas-Triviño, C. Retamal C. and K.J. Klabunde. Polymer Bull., 25, 315 (1991).
G. Cárdenas T. and J. Acuña E. Polymer Bull. 29, 1 (1992).
G. Cárdenas T., J. Acuña E., M. Rodríguez B., H. Carbacho H. Polymer Bull., 34, 31 (1995).
G. Cárdenas T., C. Retamal C. and K.J. Klabunde. Polymer Bull., 27, 383 (1992).
G. Cárdenas T., E. Salgado C. and H. González G., Polymer Bull., 35, 553 (1995).
G. Cárdenas T., E. Salgado C. and H. Carbacho H. Polymer Bull. (in press, 1996).
G. Cárdenas T. and M. González G. XXII Congreso Latinoamericano de Química, Enero 1996, pp 404.
G. Cárdenas T. and M. González G. Int. J. Polymer Mater. (in press, 1996).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Cárdenas T, G., González G, M. Metal polymers. Polymer Bulletin 37, 175–182 (1996). https://doi.org/10.1007/BF00294119
Received:
Revised:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00294119