The purpose of this study was to reduce the sintering temperature of Ba[(Ni0.6Zn0.4)0.33Nb0.67]O3 ceramics by doping with Sb2O5 and B2O3. Phase formation and dielectric properties were analyzed using X-ray diffraction and the post resonator method (10 GHz), respectively. It was observed that an addition of 1 mol % Sb2O5 or 1 mol % B2O3 was very effective in reducing the sintering temperature from 1500 to 1300 °C. However, these samples showed a temperature coefficient of resonant frequency far from 0 ppm/°C. The two additions produced a temperature coefficients with opposite signs. The combination of the two dopants produced a temperature coefficient very close to 0 ppm/°C as well as a better quality factor.
Similar content being viewed by others
References
Y. Konishi, Proc. IEEE, 79(6) (1991) 725.
J. K. Plourde and C. L. Ren, IEEE Trans. Microwave Theory and Tech., MTT-29(8) (1981) 754.
H. Ouchi and S. Kawashima, Jpn. J. Appl. Phys. 24(2) (1985) 60.
K. Wakino, T. Nishikawa, Y. Ishikawa, and H. Tamura, Br. Ceram. Trans. J. 89(1990) 39.
H. M. O'bryan, J. Thomson, and J. K. Plourde, J. Am. Ceram. Soc. 57(10) (1974) 450.
S. Y. Cho, H. J. Youn, K. S. Hong, I. T. Kim and Y. H. Kim, J. Mat. Res. 12(6) (1997).
K. Wakino, K. Minai and H. Tamura, J. Am. Ceram. Soc. 67(4) (1984) 278.
A. J. Bosman and E. E. Havinga, Phys. Rev. 129(4) (1963) 1593.
I. T. Kim, Y. H. Kim and S. J. Jung, Jpn. J. Appl. Phys. 34(8A) (1995) 4096.
Rights and permissions
About this article
Cite this article
Lee, J.H., Jang, Y.I., Youn, H.J. et al. Low-firing and microwave dielectric properties of Ba[(Ni0.6Zn0.4)0 .33Nb0.67]O3 ceramics doped with Sb2O5 and B2O3. Journal of Materials Science 34, 625–628 (1999). https://doi.org/10.1023/A:1004523502454
Issue Date:
DOI: https://doi.org/10.1023/A:1004523502454