The R-curve behaviour of a B4C-Al cermet was studied experimentally using the indentation/strength technique. Microstructural observations clearly indicate that the dominant mechanism contributing towards increasing toughness with crack length is due to bridging of ductile Al phases. It is inferred that ductile toughening, along with toughening due to residual stresses generated upon cooling of the cermet, contribute to this toughening behaviour. Close agreement between experimental results and a simple model is also established.
Similar content being viewed by others
References
L. S. Sigl, A. G. Evans, P. Mataga, R. M. Mcmeeking andB. J. Dalgleish,Acta Metall. 36 (1988) 946.
M. F. Ashby, F. J. Blunt andM. Bannister,ibid. 37 (1989) 1847.
V. V. Krstic, P. S. Nicholson andR. G. Hoagland,J. Amer. Ceram. Soc. 64 (1981) 499.
C. K. Elliott, G. R. Odette, G. E. Lucas andJ. W. Sheckherd,Mater Res. Soc. Symp. Proc. 120 (1988) 95.
A. G. Evans andR. M. Mcmeeking,Acta Metall 34 (1986) 2435.
L. S. Sigl andH. E. Exner,Metall. Trans. 18A (1987) 1299.
A. J. Pyzik, I. A. Aksay andM. Sarikaya, in “Ceramics Microstructure—1986”, Materials Science Research, edited by J. A. Pask and A. G. Evans (Plenum, New York, 1987) p. 45.
P. A. Mataga,Acta Metall. 37 (1989) 3349.
H. Hubner andW. Jillek,J. Mater. Sci. 12 (1977) 117.
R. Steinbrech, R. Khehans andW. Schaarwachter,ibid. 18 (1983) 265.
M. V. Swain,Materials Forum 13 (1989) 237.
P. Chantikul, G. R. Anstis, B. R. Lawn andD. B. Marshall,J. Amer. Ceran. Soc. 64 (1981) 539.
R. F. Krause,ibid. 71 (1988) 338.
S. Srinivasan andR. O. Scattergood,J. Mater. Res. Soc. 5 (1990) 1490.
R. F. Cook andD. R. Clark,Acta Metall 36 (1988) 555.
M. Taya, S. Hayashi, A. S. Kobayashi andH. S. Yoon,J. Amer. Ceram Soc. 73 (1990) 1382.
D. C. Halverson, A. J. Pyzik andI. A. Aksay,Proc. Ceram Engng Sci. 6 (1985) 736.
G. Dewith,J. Mater Sci. 19 (1984) 457.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Bhattacharya, A.K., Petrovic, J.J. Ductile phase toughening and R-curve behaviour in a B4C-Al cermet. J Mater Sci 27, 2205–2210 (1992). https://doi.org/10.1007/BF01117938
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01117938