Abstract
The synthesis conditions and oxygen stoichiometry were determined using a thermogravimetric analyser. The kinetics of oxygenation at different temperatures and at different atmospheres were studied. The oxygenation kinetics were found to be sensitive to porosity of the material. The appropriate oxygenation temperature was found to be 400 °C. For oxygenation temperatures below 400 °C, the oxygenation occurs by a nucleation and growth process, whereas for higher temperatures it is diffusion limited.
Similar content being viewed by others
References
J. G. Bednorz and K. A. Müller, Z. Phys. B 64 (1986) 189.
M. K. Wu, J. R. Ashburn, C. J. Torng, P. H. Hor, R. L. Meng, L. Gao, Z. J. Huang, Y. Q. Wang and C. W. Chu, Phys. Rev. Lett. 58 (1987) 908.
J. D. Jorgensen, D. G. Hinks, L. Soderholm, K. J. Volin, R. Hitterman, J. D. Grace, I. K. Schuller, C. V. Segre, K. Zhang and M. S. Klecfisch, Phys. Rev. B 36 (1987) 3608.
R. J. Cava, B. Batlogg, C. H. Chen, E. A. Rietman, S. M. Zahurak and D. Weder, ibid. 36 (1987) 5719.
D. C. Harris and T. A. Hewston, J. Solid State Chem. 69 (1987) 182.
E. H. Appelman, L. R. Morss, A. M. Kini, U. Geisser, A. Umezawa, G. W. Crabtree and K. D. Carlson, J. Inorg. Chem. 26 (1987) 3237.
J. M. Tarascon and B. G. Bagley, MRS Bull. January (1989) 53.
M. G. Langer and R. A. Dichiara, Thermochim. Acta 133 (1988) 32.
S. Jantsch, J. Ihringer, J. K. Maichle, W. Prandl, S. Kemmler-Sack, R. Kieimel, S. Losch, W. Schafee, M. Schlichenmaier and A. W. Hewat, J. Less Common Metals 150 (1989) 167.
H. M. O'bryan and P. K. Gallagher, J. Mater. Res. 3 (1988) 619.
N. McN Alford, W. J. Clegg, M. A. Harmer, J. D. Bridall, K. Kendall and D. H. Jones, Nature 332 (1988) 58.
C. Weast and M. J. Astle, “CRC Handbook of Chemistry and Physics” (CRC Press, Florida, 1981).
F. Licci, P. Tissot and H. J. Scheel, J. Less Common Metals 150 (1989) 210.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Sridharan, V., Chandran, D.R., Srinivasan, S. et al. Thermogravimetric studies of Y1Ba2Cu3O7−x superconductors. J Mater Sci 27, 4483–4488 (1992). https://doi.org/10.1007/BF00541583
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00541583