Cold-drawn copper wires were made by cold-drawing after hot-rolling tough pitch copper rods which had been pre-heated at 673–973 K. The wires were annealed at 293–673 K to study their annealing properties. The effects of pre-heating the hot-rolled tough pitch copper rods, including lead, on the recrystallization behaviour of the cold-drawn copper wires were investigated by tensile tests, electrical resistivity measurements and structural observations. The half-softening temperature of annealed cold-drawn copper wires decreased when the hot-rolled copper rods were pre-heated at 873 K before cold-drawing. This behaviour was attributed to separation of lead dissolved in the copper matrix which is known to lower the half-softening temperature.
Similar content being viewed by others
References
T. Yanagida, H. Ikeda andT. Masui,Bull. Jpn. Inst. Metals 18 (1979) 419 (in Japanese).
S. Aoyama, M. Onuki, Y. Miyake andR. Urao,J. Jpn Inst. Metals 51 (1987) 858 (in Japanese).
Idem, ibid. 52 (1988) 477 (in Japanese).
S. A. Reid andC. J. Ball,Metals Technol. 1 (1974) 412.
H.-D. Hirschfelder,Wire 28 (1978) 48.
S. Aoyama, M. Onuki, Y. Miyake andR. Urao,J. Jpn Inst. Metals 53 (1989) 94 (in Japanese).
J. S. Smart andA. A. Smith,Metals Technol. AIME Transaction Paper 1434 (1942) 1.
Idem, Trans. AIME 152 (1943) 103.
Idem, ibid., Trans. AIME 166 (1946) 144.
J. S. Smart, in “Copper: The Metal, Its Alloys and Compounds”, edited by A. Butts (Reinhold, New York, 1954) p. 410.
C. H. Pitt, P. L. Tayler andL. V. Wagoner,Metal Trans. 10A (1979) 809.
F. Schückher, A. Kosonen andL. M. Liljenvall,Scand. J. Metall. 9 (1980) 159.
S. Hori, H. Tai andH. Katayama,J. Jpn Inst. Metals 45 (1981) 1223 (in Japanese).
H. Suzuki, M. Kanno andT. Osako,ibid. 48 (1984) 854 (in Japanese).
V. J. Marino, M. Yokelson andG. J. Fischer,Wire J. 42 (1975) 60.
Y. T. Hsu andB. O'Reilly,J. Metals 29 (1977) 21.
L. K. Bigelow andH. H. Chen, in “Proceedings of the CDA-ASM Conference on Copper”, October 1972 (COD-ASM, Ohio, 1972) p. 16.
D. Coutsouradis, E. Diderrich, J. Smets, G. Crocq andL. Pauwels,Centre National de Recherches Metallurgiques 39 (1974) 73.
S. Inoue, N. Uno andM. Konuma,Hurukawadenkoziho. 66 (1979) 49 (in Japanese).
D. Müller, F. Pawlek UndH. Wever,Z. Metallkde 57 (1966) 175.
S. Aoyama, M. Onuki, Y. Miyake andR. Urao, in “Proceedings of The 100th Spring Meeting of The Japan Institute of Metals” (The Japan Institute of Metals, Tokyo, 1987) p. 200 (in Japanese).
M. Hansen andK. Anderko, in “Constitution of Binary Alloys”, 2nd Edn (McGraw Hill, New York, 1958) pp. 610, 634, 1064.
R. A. Swalin, in “Thermodynamics of Solids” (Wiley, New York, 1962) p. 88 (Japanese edition).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Aoyama, S., Onuki, M., Miyake, Y. et al. Effects of lead on annealing properties of cold-drawn copper wire. J Mater Sci 26, 3775–3779 (1991). https://doi.org/10.1007/BF01184970
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01184970