Substrate roughness, deposit thickness and the corrosion of electroless nickel coatings

  • Papers
  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

The affect of substrate roughness and coating thickness on the corrosion resistance of electroless nickel coatings on mild steel in a 0.99M Na2SO4 + 0.01 M H2SO4 + 0.05M NaCl solution has been investigated using electrochemical techniques. The coating was electrochemically more active than pure nickel. The anodic polarization, corrosion potential, and corrosion current depend on the substrate roughness and coating thickness. The substrate roughness decreased for finishes in the order, as-ground, 240 grit, 600 grit, and 1 μm diamond polish, but the corrosion current on relatively thin coatings decreased in the order 240 grit, as-ground, 600 grit, and 1 μm diamond finish. The corrosion potential and the corrosion current of coatings more than about 10μm thick were independent of the surface roughness and similar to those observed with pure nickel. The fraction porosity was estimated to be about 0.005 in a coating about 5 μm thick on a 600 SiC grit substrate.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. G. G. Gawrilov, “Chemical (Electroless) Nickel Plating”, Porcullis, Redhill, Surrey, 1979, pp. 85–90.

    Google Scholar 

  2. R. N. Duncan,Mater. Performance 22 (1983) 28.

    Google Scholar 

  3. W. J. Tomlinson andP. Gentil,Surf. Technol. 20 (1983) 149.

    Google Scholar 

  4. M. A. Trudgeon andJ. R. Griffiths,Brit. Corr. J. 21 (1986) 113.

    Google Scholar 

  5. W. J. Tomlinson andJ. P. Mayor,Surf. Engng 4 (1988) 235.

    Google Scholar 

  6. E. B. Saubestre andJ. Hajdu,Oberfaäche-Surface 9 (1968) 3, 53 (quoted in [1] p. 85).

    Google Scholar 

  7. D. J. Efros, S. V. Sharigina andN. A. Musitchuk, “Chimitescheskoe Wikelirovanie Detalej Maschin” (Gorki, ZBTI, 1958) (quoted in [1], p. 85).

    Google Scholar 

  8. M. G. Fontana, “Corrosion Engineering”, 3rd edn (McGraw-Hill, New York, 1986).

    Google Scholar 

  9. W. J. Tomlinson andS. A. Campbell,J. Mater. Sci. 21 (1986) 2590.

    Google Scholar 

  10. J. Flis andD. J. Duqette,Corrosion 41 (1985) 700.

    Google Scholar 

  11. W. J. Tomlinson, L. A. Blunt andS. Spraggett,Surf. Engng,5 (1989) 229.

    Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Rights and permissions

Reprints and permissions

About this article

Cite this article

Tomlinson, W.J., Carroll, M.W. Substrate roughness, deposit thickness and the corrosion of electroless nickel coatings. J Mater Sci 25, 4972–4976 (1990). https://doi.org/10.1007/BF00580115

Download citation

  • Received:

  • Accepted:

  • Issue Date:

  • DOI: https://doi.org/10.1007/BF00580115

Keywords

Navigation