Conclusions
The investigations into the creep and long-term strength of the iron-nickel alloy in the temperature range 873–1073°K for up to 1000 h showed that in this temperature range we can define three differing typical regions of creep strain cumulation in relation to temperature and stress. The time to failure of the batch I specimens at a temperature of 1073°K and a stress of 200 MPa in air is five times longer, than the time to failure in vacuum.
Similar content being viewed by others
Literature Cited
I. S. Tsvilyuk, E. P. Polishchuk, A. N. Badaev, and D. S. Avramenko, “Effect of alloying with nitrogen on the characteristics of long-term strength of welded joints in molybdenum-based alloys,” Probl. Prochn., No. 10, 99–103 (1983).
F. F. Khimushin, Creep-Resisting Steels and Alloys, [in Russian], Metallurgiya, Moscow (1969).
E. E. Levin and B. M. Gugelev, “Nature of the variation of the high-temperature ductility of alloys with dispersion hardening,” Metalloved. Term. Obrab. Met., No. 1, 2–5 (1967).
Additional information
Institute of Strength Problems, Academy of Sciences of the Ukrainian SSR, Kiev. Moscow, Translated from Problemy Prochnosti, No. 1, pp. 43–48, January, 1986.
Rights and permissions
About this article
Cite this article
Tsvilyuk, I.S., Rusinovich, Y.I., Rastorgueva, I.A. et al. Relationships governing deformation and failure of an iron-nickel alloy in creep in vacuum and in air. Strength Mater 18, 41–46 (1986). https://doi.org/10.1007/BF01524224
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01524224