Abstract
Due to its good physical and chemical properties, porous silicon (PSi) is very attractive to study. In this research, PSi has been fabricated on n-type Si (100) by the electrochemical anodization method. The electrolyte solution used was a mixture of HF (40%), ethanol (99%) and aquadest with volume ratio of 1:1:2, respectively. It was anodized on Si(100) surface at different current densities of 10 mA/cm2 and 20 mA/cm2 with the anodization time at each current density for 10 min, 20 min, and 30 min. The Scanning Electron Microscope (SEM) images showed that the PSi surfaces have inhomogeneous sized pores in the range of 95.00 nm–1.46 μm. The PSi layers with current density and anodization time of 10 mA/cm2 (10 min), 10mA/cm2 (20 min), and 20mA/cm2 (10 min) have spherical shaped pores while the others have some uncommon (cross sectional) shaped pores on surfaces. It is considered that the cross sectional shaped maybe caused by unstable the current during the electrochemical anodization process.
Export citation and abstract BibTeX RIS
Content from this work may be used under the terms of the Creative Commons Attribution 3.0 licence. Any further distribution of this work must maintain attribution to the author(s) and the title of the work, journal citation and DOI.