Phase equilibria in the system CaO-ZnO-B2O3 at 850°C

  • Papers
  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

Phase equilibria in the system CaO-ZnO-B2O3 were investigated at 850°C using X-ray powder diffraction techniques. The binary phases reported previously were confirmed, but no ternary phases were found. Solid solution effects were investigated for the binary phases by comparison of the patterns, whereas for calcium oxide and zinc oxide, accurate lattice parameters were compared. No solid solutions were detected.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. E. T. Carlson,J. Res. Nat. Bur. Stand. 9 (1932) 825.

    CAS  Google Scholar 

  2. B. L. Fletcher, J. R. Stevenson, andA. Whitaker,J. Amer. Ceram. Soc. 53 (1970) 95.

    CAS  Google Scholar 

  3. P. B. Hart andC. S. Brown,J. Inorg. Nuclear Chem. 24 (1962) 1057.

    Article  CAS  Google Scholar 

  4. A. Whitaker,J. Mater. Sci. 7 (1972) 189.

    Article  CAS  Google Scholar 

  5. E. R. Segnit,J. Amer. Ceram. Soc. 37 (1954) 274.

    Google Scholar 

  6. ASTM X-ray Powder Diffraction Data File, Card No. 4-0777. American Society for Testing and Materials, Philadelphia, Pennsylvania.

  7. ASTM X-ray Powder Diffraction Data File, Card No. 5-0664. American Society for Testing and Materials, Philadelphia, Pennsylvania.

  8. S. V. Berger,Acta Chem. 7 (1953) 611.

    Article  CAS  Google Scholar 

  9. F. C. Kracek, G. W. Morey, andH. E. Merwin,Amer. J. Sci. 35A (1938) 143.

    Google Scholar 

  10. D. E. Harrison andF. A. Hummel,J. Electrochem Soc. 103 (1956) 491.

    Google Scholar 

  11. H. Bauer,Z. anorg. Chem. 320 (1963) 306.

    Article  CAS  Google Scholar 

  12. J. Fayos, S. García-Blanco, andL. Rivoir,Anales Real Soc. Españ. Fís. Quím. 62A (1966) 297.

    Google Scholar 

  13. H. E. Swanson andE. Tatge J. Res. Nat. Bur. Stand. 46 (1951) 318.

    CAS  Google Scholar 

  14. Yu. s. Leonov,Doklady Akad. Nauk. S.S.S.R. 114 (1957) 976. See alsoSoviet Physiks “Doklady” 2 (1957) 261.

    CAS  Google Scholar 

  15. Idem, Zhur. neorg. Khim. 3 (1958) 1245.

    CAS  Google Scholar 

  16. J. B. Nelson andD. P. Riley,Proc. Phys. Soc. Lond. 57 (1945) 160.

    Article  CAS  Google Scholar 

  17. E. Wait,Technol. Report AERE-R3598 (1961).

  18. L. H. Van Vlack, “physical Ceramics for Engineers” (Addison-Wesley Publishing Co. Inc., Reading, Massachusetts, 1964) 52.

    Google Scholar 

  19. Idem, ibid, 302.

    Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Rights and permissions

Reprints and permissions

About this article

Cite this article

Whitaker, A., Borton, D.F. Phase equilibria in the system CaO-ZnO-B2O3 at 850°C. J Mater Sci 7, 194–197 (1972). https://doi.org/10.1007/BF02403507

Download citation

  • Received:

  • Accepted:

  • Issue Date:

  • DOI: https://doi.org/10.1007/BF02403507

Keywords

Navigation