Abstract
Fine β-SiC powders either pure or with the addition of 1 wt % of α-SiC particles acting as a seeding medium, were hot-pressed at 1800 °C for 1 h using Y2O3 and Al2O3 as sintering aids and were subsequently annealed at 1900 °C for 2, 4 and 8 h. During the subsequent heat treatment, the β → α phase transformation of SiC produced a microstructure of “in situ composites” as a result of the growth of elongated large α-SiC grains. The introduction of α-SiC seeds into the β-SiC accelerated the grain growth of elongated large grains during annealing which led to a coarser microstructure. The sample strength values decreased as the grain size and fracture toughness continued to increase beyond the level where clusters of grains act as fracture origins. The average strength of the in situ-toughened SiC materials was in the range of 468–667 MPa at room temperature and 476–592 MPa at 900 °C. Typical fracture toughness values of 8 h annealed materials were 6.0 MPa m1/2 for materials containing α-SiC seeds and 5.8 MPa m1/2 for pure β-SiC samples.
Similar content being viewed by others
References
S. PROCHAZKA, in “Special Ceramics 6,” edited by P. Popper (British Ceramic Research Association, Manchester, 1975) p. 171.
Y. W. KIM and J. G. LEE, J. Mater. Sci. 27 (1992) 4746.
J. B. HURST and S. DUTTA, J. Amer. Ceram. Soc. 70 (1987) C-303.
S. DUTTA, ibid 71 (1988) C-474.
N. P. PADTURE, ibid 77 (1994) 519.
N. P. PADTURE and B. R. LAWN, ibid 77 (1994) 2518.
V. D. KRSTIC, MRS Bull. 20 (1995) 46.
M. A. MULLA and V. D. KRSTIC, Acta Metall. Mater. 42 (1994) 303.
S. K. LEE and C. H. KIM, J. Amer. Ceram. Soc. 77 (1994) 1655.
Y. W. KIM, M. MITOMO and H. HIROTSURU, ibid 78 (1995) 3145.
W. J. KIM and Y. W. KIM, J. Kor. Ceram. Soc. 32 (1995) 1162.
Y. W. KIM, K. S. CHO and J. G. LEE, Kor. J. Ceram. 2 (1996) 39.
S. K. LEE, D. K. KIM and C. H. KIM, J. Amer. Ceram. Soc. 78 (1995) 65.
T. NOSE and T. FUJII, ibid 71 (1988) 328.
Y. W. KIM, H. TANAKA, M. MITOMO and S. OTANI, J. Ceram. Soc. Jpn. 103 (1995) 257.
Y. W. KIM and J. G. LEE, J. Amer. Ceram. Soc. 72 (1989) 1333.
L. S. SIGL and H. J. KLEEBE, ibid 76 (1993) 773.
L. U. OGBUJI, T. E. MITCHELL, A. H. HEUER and S. SHINOZAKI, ibid 64 (1981) 100.
L. U. OGBUJI, T. E. MITCHELL and A. H. HEUER, ibid 64 (1981) 91.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Cho, DH., Kim, YW. & Kim, W. Strength and fracture toughness of in situ-toughened silicon carbide. Journal of Materials Science 32, 4777–4782 (1997). https://doi.org/10.1023/A:1018635131661
Published:
Issue Date:
DOI: https://doi.org/10.1023/A:1018635131661