The effect of annealing conditions on the superconductivity of the Pb-based 1 2 1 2 phase Pb0.65Sr2.35Y0.5Ca0.5Cu2O y system was studied. The weight change of the samples was measured by thermogravimetric analysis (TGA). The phases occurring in the samples were detected by X-ray diffraction (XRD) and their superconducting transitions were determined by alternating current (a.c.) susceptibility measurements. The results showed that the oxygen occupancy sites of the samples annealed under various conditions were different, and the oxygen content or oxygen occupancy site affected the phase formation of the sample. It has been found that there is an optimum value of oxygen content at which TC is the highest, and the highest TC can be obtained only within a very narrow range of oxygen content.
Similar content being viewed by others
References
A. ONO and Y. UCHIDA, Jpn. J. Appl. Phys. 29 (1990) L586.
X. X. TANG, D. E. MORRIS and A. P. B. SINHA, Phys. Rev. B 43 (1991) 7936.
T. ROUILLON, J. PROVEST, M. HERVIEU, D. GROULT, C. MICHEL and B. RAVEAU, Physica C 171 (1990) 7.
H. B. LIU, D. E. MORRIS and A. P. B. SINHA, ibid. 204 (1993) 262.
W. WIDDER, M. FRANZ, L. BAUERNFEIND and H. F. BRAUN, ibid. 217 (1993) 121.
H. JIN, N. L. WANG, Y. CHONG, M. DENG, K. Q. RUAN, L. Z. CAO and Z. J. CHEN, ibid. 231 (1994) 167.
TOSHIHIKO MAEDA, KAZUHIRO SAKUYAMA, FUJIO IZUMI, H. YAMAUCHI, HAJIME ASANO and SHOJI TANAKA, ibid. 175 (1991) 393.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
JIN, H., RUAN, K.Q., WANG, L.B. et al. Annealing dependence of the superconductivity of Pb0.65Sr2.35Y0.5Ca0.5Cu2Oy. Journal of Materials Science 32, 4623–4626 (1997). https://doi.org/10.1023/A:1018641805737
Issue Date:
DOI: https://doi.org/10.1023/A:1018641805737