Experimental results are presented on the measurements of thermal expansion (up to 1500°C), thermal conductivity (up to 1000°C), dielectric constant (up to 450 °C) and tanδ (up to 800 °C) of zirconyl phosphate compacts obtained by sintering at 1600°C. The thermal expansion coefficient of the samples at the temperature below 1100°C was less than 1.7 × 10−6°C−1. The samples showed a definite shrinkage at temperatures of 1110 and 1470°C due to the phase transformations. The expansion at 1500°C was less than that at 1100°C probably because of the phase transformation. The thermal conductivity at room temperature was a very small value (0.0046 to 0.0065 cal s−1 cm°C−1 cm−2). The dielectric constant was close to 9. The value of tan° (−0.0001) measured is one of the lowest values for ceramic materials.
Similar content being viewed by others
References
D. E. Harrison, H. A. McKinley and F. A. Hummel, J. Amer. Ceram. Soc. 37 (1954) 277.
I. Yamai and T. Oota, ibid. 68 (1985) 273.
Idem, ibid. 68 (1987) 585.
M. Omori, K. C. Hsu, T. Hirai and T. Fukuda, “Material Science Forum”, 34/36 Proceeding of the International Ceramics Conference and Exhibition-AUSTCERAM88, 1988, Sydney, Australia (Trans. Tech. Publ., USA, 1988) p. 851.
W. Schreyer and J. F. Schairer, J. Petrology 2 (1961) 324.
J. H. Koenig, “Materials in Design Engineering”, May (Reader Service Dept., New York, 1958) p. 121.
W. J. Parker, R. J. Jenkins, C. P. Butler and G. L. Abbott, J. Appl. Phys. 32 (1961) 1679.
W. Gebert and E. Tillmanns, Acta Crystallogr. B31 (1975) 1768.
K. C. Hsu, M. Eng. Thesis, Tohoku University, Japan (1989).
E. P. Meagher and G. V. Gibbs, Can. Mineral. 15 (1977) 43.
H. Ikawa, T. Otagi, O. Imai, M. Suzuki, K. Urabe and S. Udagawa, J. Amer. Ceram. Soc. 69 (1986) 492.
W. Fix, H. Heymam and R. Heinke, ibid. 52 (1969) 346.
M. Mathew, L. W. Schroeder, B. Dickens and W. E. Brown, Acta Crystallogr. B33 (1977) 1325.
W. R. Beck, J. Amer. Ceram. Soc. 32 (1949) 147.
E. C. Shafer and R. Roy, Z. Phys. 11 (1957) 30.
W. D. Kingery, H. K. Bowen and D. R. Uhlmann, “Introduction to Ceramics”; 2nd Edition (John Wiley, New York, 1976) Chap. 12.
W. D. Kingery and M. C. McQuarrie, J. Amer. Ceram. Soc. 37 (1954) 67.
W. D. Kingery, H. K. Bowen and D. R. Uhlmann, “Introduction to Ceramics”, 2nd Edition (John Wiley, New York, 1976) Chap. 18.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Omori, M., Hsu, K.C., Tsunekawa, S. et al. Thermal and dielectric properties of zirconyl phosphate compact. J Mater Sci 27, 408–412 (1992). https://doi.org/10.1007/BF00543930
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00543930