Abstract
Ti-6A1-4V shows distinct active-passive behaviour in phosphoric acid over a wide concentration range. The cathodic polarization curves are similar over a wide range of acid concentration and temperatures. The alloy undergoes active dissolution and turns passive in the negative potential region followed by a wide range of passivity at all acid concentrations at different temperatures. Increasing acid concentration up to 11 M results in an increase in critical current density (i cr). The passive current density (i p) increases up to an acid concentration of 9 M while at 13 M i cr and i p decrease appreciably. A significant increase in both i cr and i p occurs with increase in solution temperature. The passive specimen remained stable for a long time when exposed to phosphoric acid under open circuit conditions.
Similar content being viewed by others
References
L. J. Barron, Light Metal Age 14 (1956) 16.
Y. Ishu and Y. Hoskino, Chem. Eng., Tokyo 21 (1957) 559.
V. S. Ivins, Power Eng. 69 (1965) 52.
E. L. Owen, R. C. May, F. H. Beck and M. G. Fontana, Corrosion 28 (1972) 292.
R. S. Glass and Y. Ki Kong, Electrochim. Acta 29 (1984) 1465.
A. A. Mazhar, F. El Taib Haekal and A. G. Gad Allah, Corrosion 44 (1988) 705.
N. N. Rao and V. B. Singh, Corros. Sci. 25 (1985) 144.
V. K. Singh and V. B. Singh, ibid. 28 (1988) 385.
Idem, Corrosion 43 (1987) 756.
V. B. Singh and V. K. Singh, J. Material Sci. 26 (1990) 690.
E. J. Kelly and H. R. Bronstein, J. Electrochem. Soc. 131 (1984) 223.
Pu Suyern and Ji Shuda, 10th International Congress on Metallic Corrosion (Madras) IV (1987) 3815.
S. M. A. Hosseini and V. B. Singh, Mater. Chem. Phys. 33 (1993) 63.
V. B. Singh and S. M. A. Hosseini, Corros. Sci. 34 (1993) 1723.
D. D. N. Singh, J. Electrochem. Soc. 132 (1985) 378.
D. T. Chin and H. H. Chang, J. Appl. Electrochem. 19 (1989) 95.
V. B. Singh and S. M. A. Hosseini, unpublished work.
S. M. A. Hosseini and V. B. Singh, MS submitted for publication in J. Mater. Sci.
J. C. Griess Jr., Corrosion 24 (1968) 96.
F. El Taib Heakel, A. S. Mogoda, A. A. Mazhar and M. S. El Bassiong, Corros. Sci. 27 (1987) 453.
L. Young, Trans. Faraday Sci. 51 (1955) 1250.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Singh, V.B., Hosseini, S.M.A. Corrosion behaviour of Ti-6Al-4V in phosphoric acid. J Appl Electrochem 24, 250–255 (1994). https://doi.org/10.1007/BF00242892
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF00242892