It is well known that X-ray diffraction is one of the most powerful means for investigating the microscopic structure of crystalline materials. X-ray diffraction is advantageous when it is applied to metallic materials; it responds very sensitively to changes in the metal's crystalline structure. Another characteristic advantage of the X-ray-diffraction approach is its nondestructive nature in the measurement of crystalline-material parameters, enabling us to observe the process of mechanical phenomena of metals, such as fatigue and creep.
The X-ray-diffraction patterns obtained on a deformed material include a great deal of information covering the microscopic and macroscopic characters consistent with the nature of the existing material. Residual stress measured by means of X ray is called the macroscopic-material parameter. It is evaluated by measuring the shift of the peak of a diffraction profile. The diffusiveness of the profile corresponds to the irregularity in microscopic structure of deformed crystalline material and it is noted as the submacroscopic material parameter. The X-ray-microbeam diffraction technique supplies information on the change in microscopic structure such as subgrain size, misorientation and microlattice strain. Profile analysis is another way to evaluate the microscopic-material parameters: particle size and microscopic strain.
By appropriately combining these techniques in the study of mechanical behavior of materials, the parameters that control the phenomena may be extracted to facilitate discussion of their mechanism. In this lecture, X-ray-diffraction techniques to evaluate the macroscopic, submacroscopic and microscopic-material parameters are presented and the approach is demonstrated by exhibiting a case of studies on fatigue and creep of carbon steels at room and elevated temperature, where phenomena are discussed in terms of the change in the material parameters. Initiation and propagation of fatigue crack in steel at room temperature, the change in microstructure during isothermal and thermal fatigue, and also that in creep at elevated temperature under variational load are presented.
Similar content being viewed by others
References
Taira, S., “X-Ray Approach for the Study on Mechanical Behavior of Metals,” Proc. Int. Conf. on Mech. Behav. Mat., Kyoto, Special Volume, 111 (1972).
J. of the Soc. of Mat. Sci., Japan,11,629–718 (1962);12,829–911 (1963);13,905–1012 (1964);14,923–1029 (1965);15,813–901 (1966);16,921–1041 (1967);17,1047–1180 (1968);18,1033–1156 (1969);19,1011–1141 (1970);20,1239–1360 (1971);21,1045–1171 (1972).
Aoyama, S., Satta, K. andTada, M., “The Effect of Setting Errors on the Accuracy of Stress Measured with Parallel Beam X-Ray Diffractometer,”J. Soc. Mat. Sci., Japan,17,1071 (1968).
Karashima, S., Shimatani, K. andSugisawa, S., “The X-Ray Study of Residual Stresses in Extended Brass Specimens by Means of a Diffractometer,”J. Soc. Mat. Sci., Japan,13,938 (1964).
Ishii, K., Iwamoto, M., Shiraiwa, T. and Sakamoto, Y., Residual Stress in the Induction Hardened Surface of Steel, SAE SP-362 (710280) (1968).
Hayashi, K., X-Ray Investigation on Lattice Strain and Deformation of Polycrystalline Metals, Doctor's Thesis, Kyoto Univ. (1970).
Taira, S. Hayashi, K. and Koe, S., Anisotropy and Residual Lattice Strains Induced in Steel Sheet by Plastic Deformation, “X-Ray Study on Strength and Deformation,” J. Soc. of Med. Sci., Japan, 23 (1970).
Namikawa, H., Doctor's Thesis, Kyoto Univ. (1972).
Wolfstieg, U., “Röntgenographische Spannungsmessungen mit breiten Linien, Arch. Eisenhüttenwes.,30,447 (1959).
Taira, S. andHonda, K., “X-Ray Investigation on the Fatigue Damage of Metals,”Bull. of ISME,4,230 (1961).
Taira, S., Honda, K. andMatsuki, K., “X-Ray Investigation of Fatigue Damage of Metals (On the Changes in Half-Value Breadth of X-Ray Diffraction Line, Residual Stress, Micro-Structure, and Micro-Hardness Due to Stress Repetitions),”Trans. JSME,28,1325 (1962).
Ohuchida, H., Nishioka, A. andNagao, M., “Size Effect on Fatigue Strength of Carbon Steel Machined by a Lathe (X-Ray Detection of Fatigue Damage in Machine Parts),”Trans. JSME,38,1925 (1972).
Hirsch, P. B. and Kellar, J. N. “A Study of Cold-Worked Aluminium by an X-Ray Micro-Beam Technique, I. Measurement of Particle Volume and Misorientations, Acta Cryst.,5,162; Hirsch, P. B., “A Study of Cold-Worked Aluminium by an X-Ray Micro-Beam Technique, II. Measurement of Shape of Spots, and III. The Structure of Cold-Worked Aluminium,” Acta Cryst.,5,168.
Taira, S. andHayashi, K., “X-Ray Study on Fatigue of Mild-Steel (On the Feature of Fatigue Mechanism in Comparison with Other Modes of Fracturing),”Trans. Iron & Steel Inst., Japan,8,220 (1968);Hayashi, K., “X-Ray Study of Micro-structural Change due to Fatigue of Low Carbon Steel,” Proc. Int. Conf. on Mech. Behav. Mat., Kyoto,2,26 (1972).
Taira, S. andHayashi, K., “X-Ray Investigation on Fatigue Fracture of Notched Steel Specimen (Observation of Fatigue Phenomenon of Annealed Low-Carbon Steel by X-Ray Microbeam Technique),”Bull. of JSME,9,627 (1966).
Taira, S., Hayashi, K. and Tanaka, K., “X-Ray Investigation on Fatigue Fracture of Noteched Specimens (Investigation on Fatigue Process of Cold-Rolled or Quench-Aged Low-Carbon Steel Specimens),” Proc. 11th Japan Cong. Mat. Res., 18 (1968).
Warren, B. E. andAverbach, B. L., “The Effect of Cold-Work Distortion on X-Ray Patterns,”J. Appl. Phys.,21,595 (1950).
Hall, W. H., “X-Ray Line Broadening in Metals,”Proc. Phys. Soc.,A-62,741 (1949).
Taira, S., Goto, T. andNakano, Y., “X-Ray Investigation of Low-Cycle Fatigue in an Annealed Low-Carbon Steel,”J. Soc. Mat. Sci., Japan,17,1135 (1968).
Taira, S. andTanaka, K., “Study of Fatigue Crack Propagation by X-ray Diffraction Approach,”Eng. Frac. Mech.,4,925 (1972).
Taira, S. andTanaka, K., “Microscopic Study of Fatigue Crack Propagation in Carbon Steels,”Proc. Int. Conf. on Mech. Behav. Mat., Kyoto,2,48 (1972).
Rice, J. R., “Mechanism of Crack Tip Deformation and Extension by Fatigue,”ASTM Spec. Tech. Publ., 415, 247 (1967).
Taira, S. andFujino, M. et al, “Distinctive Feature of Fatigue Crack Application to Estimating Fatigue Life for Two Step Temperature Test,”J. Soc. Mat. Sci., Japan,22,70 (1973).
Taira, S., “Thermal Fatigue and Its Relation to Creep Rupture and Mechanical Fatigue,” Proc. 3rd Symp. Nav. Stru. Mech., New York, 187 (1963).
Taira, S. and Inoue, T., “Thermal Fatigue under Multiaxial Thermal Stresses,” Proc. Int. Conf. Therm. Str. & Therm. Fatigue, Berkeley England, 66 (1969).
Taira, S., “Relation Between Thermal Fatigue and Low-Cycle Fatigue at Elevated Temperature,” preprint Symp. Fatigue Elev. Temp. (1972); to be published ASTM STP.
Taira, S., Fujino, M. andHaji, T., “Effect of Mean Temperature and Temperature Range on Thermal Fatigue Strength of a Low Carbon Steel,”J. Soc. Mat. Sci., Japan,22,63 (1973).
Taira, S., Nakanishi, E. and Kato, K., “X-Ray Investigation of Creep Under Intermittent Load (In the Case of Long Period Stress Cycle),” Proc. 12th Japan Cong. Mat. Res., 35 (1969).
Ellison, E. G., “A Review of the Interaction on Creep and Fatigue,”J. Mech. Eng. Sci.,11 (3),318 (1969).
Taira, S., Fujino, M. and Inohara, M., “Internal Stress and Microstructure of a Low Carbon Steel During Creep Deformation at Elevated Temperature,” J. Soc. Mat. Sci., Japan, to be published.
Taira, S. andFujino, M., “Mechanical Behavior of Low Carbon Steels at Blue-brittleness Temperature Range,”Proc. Int. Conf. on Mech. Behav. Mat., Kyoto,1,117 (1972).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Taira, S. X-ray-diffraction approach for studies on fatigue and creep. Experimental Mechanics 13, 449–463 (1973). https://doi.org/10.1007/BF02322729
Issue Date:
DOI: https://doi.org/10.1007/BF02322729