Abstract
Two chemical routes were employed to prepare Si-Ti polymers, using acetylacetone (acacH) and acetic acid (HOAc) as modifying agents. The homogeneous and transparent sols were studied at different aging times. The characterization techniques were 29Si NMR, FTIR, UV-Vis and TGA. When HOAc was used, the oligomeric species in the first stages of polymerization were assigned by 29Si NMR. The Ti–O–Si bond vibration was detected by FTIR in the 950–960 cm–1 region. UV-Vis spectroscopy showed bands of acac bonded to Ti at 300 nm and 365 nm, and OAc– bonded to Ti was found at 320 nm. The TGA study allowed the establishment of the xerogel formulas.
Similar content being viewed by others
References
C.J. Brinker and G.W. Scherer, Sol-Gel Science, The Physics and Chemistry of Sol-Gel Processing (Academic Press, San Diego, CA, 1990).
J. Méndez-Vivar and C.J. Brinker, J. Sol-Gel Sci. Tech. 2, 393 (1994).
J.F. Basil and C.C. Lin, in UltrastructureProcessing of Advanced Ceramics, edited by J.F. Mackenzie and D.R. Ulrich (Wiley, NY, 1988), p. 783.
C. Wies, K. Meise-Gresch, W. Muller-Warmuth, W. Beier, A.A. Goktas, and G.H. Frischat, Ber. Bunsenges. Phys. Chem. 92, 689 (1988).
C.C. Lin and J.F. Basil, in Better Ceramics Through Chemistry, edited by C.J. Brinker, F.E. Clark, and F.R. Ulrich (Mat. Res. Soc. Symp. Proc., Pittsburgh, PA, 1986), Vol. 73, p. 585.
L.W. Kelts and N.J. Armstrong, in Better Ceramics Through Chemistry, edited by C.J. Brinker, F.E. Clark, and F.R. Ulrich (Mat. Res. Soc. Symp. Proc., Pittsburgh, PA, 1988), Vol. 121, p. 519.
S. Prabakar, R.A. Assink, N.K. Raman, and C.J. Brinker, in Better Ceramics Through Chemistry VI, edited by A.K. Cheetham, C.J. Brinker, M.L. Mecartney, and C. Sanchez (Mat. Res. Soc. Symp. Proc., Pittsburgh, PA, 1994), Vol. 346, p. 979.
S. Purohit, P. Koley, L.S. Prasad, P.T. Manoharan, and S. Ghosh, Inorg. Chem. 28, 3735 (1989).
K. Nakamoto, Infrared and Raman Spectra of Inorganic and Coordination Compounds (John Wiley, USA, 1978).
J. Méndez-Vivar, A. Campero, J. Livage, and C. Sanchez, J. Non-Cryst. Solids 121, 26 (1990).
A. Yamamoto and S. Kambara, J. Am. Chem. Soc. 79, 4344 (1957).
C. Sanchez, F. Babonneau, S. Doeuff, and A. Leaustic, in Ref. 3, p. 77.
T. López, J. Méndez, T. Zamudio, and M. Villa, Mat. Chem. Phys. 30, 161 (1992).
D.P. Partlow and B.E. Yoldas, J. Non-Cryst. Solids 46, 153 (1981).
A. Léaustic, F. Babonneau, and J. Livage, Chem. Mat. 1, 240 (1989).
M. Beghi, P. Chiurlo, L. Costa, M. Palladino, and M.F. Pirini, J. Non-Cryst. Solids 145, 175 (1992).
A. Campero, R. Arroyo, C. Sanchez, and J. Livage, in Ref. 3, p. 327.
K.H. von Thiele and M. Panse, Z. Anorg. Alls. Chem. 441, 23 (1978).
A. Léaustic, F. Babonneau, and J. Livage, Chem. Mater. 1, 248 (1989).
W.C. LaCourse and S. Kim, Ceram. Eng. Sci. Proc. 8, 1128 (1987).
Rights and permissions
About this article
Cite this article
Méndez-Vivar, J., Mendoza-Serna, R., Gómez-Lara, J. et al. Spectroscopic Study of SiO2-TiO2 Sols Prepared Using Stabilizing Agents. Journal of Sol-Gel Science and Technology 8, 235–241 (1997). https://doi.org/10.1023/A:1026441709416
Issue Date:
DOI: https://doi.org/10.1023/A:1026441709416