Abstract
In the present article, the reactions and phase transformations occurring between the fibers and the matrix during the T6 thermal treatment of an industrial composite are analyzed. The composite (taken from prototype diesel piston heads) consisted of an aluminum alloy conforming to AFNOR AS12UNG (Al-12 pct Si-1 pct Mg-1 pct Cu-1 pct Ni) that was reinforced with SAFFIL δ-alumina short fibers. Different heat-treating temperatures, holding times, and heating rates were considered. As a result of all these treatments, small to medium size (between 1 to 10 µm) holes were observed at the matrixfiber interfaces, although the amount and size varied depending on the heat-treating conditions. This porosity was attributed to the volume contraction associated with the reaction between the silica contained in the preform (colloidal silica is the binder for the alumina fibres) and the magnesium present in the aluminum alloy to produce MgO and Si during the solution heating treatment. This local volume contraction is higher than 28 pct.
Similar content being viewed by others
References
S. Rawal: JOM, vol. 53(4), p. 14.
Y.C. Chen and Y.C. Fann: MRL Bull. Res. Dev., 1992, vol. 6 (1), pp. 97–101.
J. Bär, H.-J. Gudladt, J. Illy, and J. Lendvai: Mater. Sci. Eng., 1998, vol. A248, pp. 181–86.
C.M. Friend, I. Horsffall, S.D. Luxton, and R.I. Young: in Cast Reinforced Metal Composites, S.G. Fishman and A.K. Dhingra, eds., ASM INTERNATIONAL, Metals Park, OH, 1988, pp. 309–15.
A.D. Mc Leod and C.M. Gabryel: Metall. Trans. A, 1992, vol. 23A, pp. 1279–83.
J.C. Lee, G.H. Kim, and H.I. Lee: Mater. Sci. Technol., 1997, vol. 13, pp. 182–86.
T. Christman and S. Suresh: Mater. Sci. Eng., 1988 vol. A102, pp. 211–16.
P. Appendino, C. Badini, F. Marino, and A. Tomas: Mater. Sci. Eng., 1991, vol. A35, pp. 275–77.
B. Dutta and M.K. Surappa: Scripta Metall. Mater., 1995, vol. 32, pp. 731–33.
A. García-Romero: Doctoral Thesis, Universitat Politécnica de Catalunya, 1996, (in Spanish).
Barcelona, CRC Handbook of Chemistry and Physics, 61st ed., R.C. Weast, ed., CRC Press Inc., Boca Raton, FL, 1980.
Phase Diagrams of Binary Magnesium Alloys, A.A. Nayeb-Hashemi and J.B. Clark, eds., ASM INTERNATIONAL, Metals Park, OH, 1988.
Handbook of Properties of Technical and Engineering Ceramics, Part I. An Introduction for the Engineer and Designer, R. Morrell, ed., The Stationery Office Books, London, 1985.
A. García-Romero, A.M. Irisarri, and M. Anglada: 9th Int. Conf. on the Mechanical Behaviour of Materials ICM9, Geneva, May 2003.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
García-Romero, A., Irisarri, A.M., Anglada, M. et al. Study of the porosity produced in an aluminum alloy matrix composite due to a T6 heat treatment. Metall Mater Trans A 35, 2503–2510 (2004). https://doi.org/10.1007/s11661-006-0230-8
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-006-0230-8