Effect of rotation speed on microstructure and mechanical properties of refill friction stir spot welded 6061-T6 aluminum alloy

  • ORIGINAL ARTICLE
  • Published:
The International Journal of Advanced Manufacturing Technology Aims and scope Submit manuscript

Abstract

Refill friction stir spot welding (RFSSW) has been used to weld 6061-T6 aluminum alloy, and keyhole free joints were successfully obtained. Effect of tool rotation speed on microstructure and mechanical properties of joint was investigated. The joint was divided into four zones, i.e., the base material (BM), heat-affected zone (HAZ), thermo-mechanically affected zone (TMAZ), and stir zone (SZ) according to microstructural evolution. Defect was not found on the surface of welded joint, but inner defects of partial bonding, bonding ligament, hook, and voids were observed within the welded joint. The microhardness of HAZ and TMAZ was lower than that of the BM, while the maximum microhardness was obtained in the SZ of welded joints. With increasing tool rotation speed from 1100 to 1700 rpm, microhardness decreased with increasing grain size in the weld. The maximum tensile shear failure load of 7522 N was obtained for the joint under tool rotation speed of 1500 rpm. Two different failure modes of plug fracture and tensile-shear mixed fracture were observed during the tensile shear tests.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Iwashita T (2003) Method and apparatus for joining. US Patent 6601751:B2

    Google Scholar 

  2. Schilling C, Dos Santos JF (2001) Method and device for linking at least two adjoining work pieces by friction welding. US Patent 6722556:B2

    Google Scholar 

  3. Li Z, Ji S, Ma Y, Yue Y, Gao S (2016) Fracture mechanism of refill friction stir spot-welded 2024-T4 aluminum alloy. Int J Adv Manuf Technol 86(5–8):1925–1932

    Article  Google Scholar 

  4. Amancio-Filho ST, Camillo APC, Bergmann L, dos Santos JF, Kury SE, Machado NGA (2011) Preliminary investigation of the microstructure and mechanical behaviour of 2024 aluminium alloy friction spot welds. Mater Trans 52(5):985–991

    Article  Google Scholar 

  5. Tier MD, Rosendo TS, dos Santos JF, Huber H, Mazzaferro JA, Mazzaferro CP, Strohaecker TR (2013) The influence of refill FSSW parameters on the microstructure and shear strength of 5042 aluminium welds. J Mater Process Technol 213(6):997–1005

    Article  Google Scholar 

  6. Cao JY, Wang M, Kong L, Guo LJ (2016) Hook formation and mechanical properties of friction spot welding in alloy 6061-T6. J Mater Process Technol 230:254–262

    Article  Google Scholar 

  7. Shen Z, Yang X, Yang S, Zhang Z, Yin Y (2014) Microstructure and mechanical properties of friction spot welded 6061-T4 aluminum alloy. Mater Des 54:766–778

    Article  Google Scholar 

  8. Uematsu Y, Tokaji K, Tozaki Y, Kurita T, Murata S (2008) Effect of re-filling probe hole on tensile failure and fatigue behaviour of friction stir spot welded joints in Al–Mg–Si alloy. Int J Fatigue 30(10–11):1956–1966

    Article  Google Scholar 

  9. Rosendo T, Parra B, Tier MAD, da Silva A, dos Santos JF, Strohaecker TR (2011) Mechanical and microstructural investigation of friction spot welded AA6181-T4 aluminium alloy. Mater Des 32(3):1094–1100

    Article  Google Scholar 

  10. Rosendo T, Tier M, Mazzaferro J, Mazzaferro C, Strohaecker TR, dos Santos JF (2015) Mechanical performance of AA6181 refill friction spot welds under lap shear tensile loading: mechanical performance of aa6181 refill friction spot welds under lap shear tensile loading. Fatigue Fract Eng Mater Struct 38(12):1443–1455

    Article  Google Scholar 

  11. Zhao YQ, Liu HJ, Chen SX, Liu Z, Hou JC (2014) Effects of sleeve plunge depth on microstructures and mechanical properties of friction spot welded Alclad 7B04-T74 aluminum alloy. Mater Des 62:40–46

    Article  Google Scholar 

  12. Zhao YQ, Liu HJ, Lin Z, Chen SX, Hou CJ (2014) Microstructures and mechanical properties of friction spot welded Alclad 7B04-T74 aluminium alloy. Sci Technol Weld Join 19(7):617–622

    Article  Google Scholar 

  13. Zhao Y, Liu H, Yang T, Liu Z, Hu Y (2016) Study of temperature and material flow during friction spot welding of 7B04-T74 aluminum alloy. Int J Adv Manuf Technol 83(9–12):1467–1475

    Article  Google Scholar 

  14. Shen Z, Yang X, Zhang Z, Cui L, Li T (2013) Microstructure and failure mechanisms of refill friction stir spot welded 7075-T6 aluminum alloy joints. Mater Des 44:476–486

    Article  Google Scholar 

  15. Shen Z, Yang X, Zhang Z, Cui L, Yin Y (2013) Mechanical properties and failure mechanisms of friction stir spot welds of AA 6061-T4 sheets. Mater Des 49:181–191

    Article  Google Scholar 

  16. Tier MD, Rosendo TS, Mazzaferro JA, Mazzaferro CP, dos Santos JF, Strohaecker TR (2016) The weld interface for friction spot welded 5052 aluminium alloy. Int J Adv Manuf Technol 1–10

  17. Yin YH, Ikuta A, North TH (2010) Microstructural features and mechanical properties of AM60 and AZ31 friction stir spot welds. Mater Des 31(10):4764–4776

    Article  Google Scholar 

  18. Badarinarayan H, Shi Y, Li X, Okamoto K (2009) Effect of tool geometry on hook formation and static strength of friction stir spot welded aluminum 5754-O sheets. Int J Mach Tools Manuf 49(11):814–823

    Article  Google Scholar 

  19. Oliveira PHF, Amancio-Filho ST, dos Santos JF, Hage E Jr (2010) Preliminary study on the feasibility of friction spot welding in PMMA. Mater Lett 64(19):2098–2101

    Article  Google Scholar 

  20. Mishra RS, Ma ZY (2005) Friction stir welding and processing. Mater Sci Eng R Rep 50:1–78

    Article  Google Scholar 

  21. Rodrigues DM, Loureiro A, Leitao C, Leal RM, Chaparro BM, Vilaca P (2009) Influence of friction stir welding parameters on the microstructural and mechanical properties of AA 6016-T4 thin welds. Mater Des 30(6):1913–1921

    Article  Google Scholar 

  22. Su P, Gerlich A, North TH, Bendzsak GJ (2013) Energy utilisation and generation during friction stir spot welding. Sci Technol Weld Join 11(2):163–169

    Article  Google Scholar 

  23. Effertz PS, Infante V, Quintino L, Sunhuddin U, Hanke S, dos Santos JF (2016) Fatigue life assessment of friction spot welded 7050-T76 aluminium alloy using Weibull distribution. Int J Fatigue 87:381–390

    Article  Google Scholar 

  24. Ji SD, Wang Y, Zhang J, Li Z (2016) Influence of rotating speed on microstructure and peel strength of friction spot welded 2024-T4 aluminum alloy. Int J Adv Manuf Technol 1–7

Download references

Author information

Authors and Affiliations

  1. Shandong Provincial Key Laboratory of Special Welding Technology, Harbin Institute of Technology at Weihai, Weihai, 264209, People’s Republic of China

    L. Zhou, L. Y. Luo, T. P. Zhang, W. X. He & J. C. Feng

  2. State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, People’s Republic of China

    L. Zhou, Y. X. Huang & J. C. Feng

Authors
  1. L. Zhou
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. L. Y. Luo
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. T. P. Zhang
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. W. X. He
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Y. X. Huang
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. J. C. Feng
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to L. Zhou.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Zhou, L., Luo, L.Y., Zhang, T.P. et al. Effect of rotation speed on microstructure and mechanical properties of refill friction stir spot welded 6061-T6 aluminum alloy. Int J Adv Manuf Technol 92, 3425–3433 (2017). https://doi.org/10.1007/s00170-017-0359-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00170-017-0359-1

Keywords

Search

Navigation