Abstract
Aqueous solutions of xAl(NO3)3 + (1−x)Cr(NO3)3 were used for electrodeposition of ceramic Al2O3–Cr2O3 alloy coatings on TiC, TiB2 and SiC substrates. Cell voltage and deposit weight were studied as function of deposition duration, current density and electrolyte composition. It was shown that the electrochemical parameters permit simple control of the deposition process. Optimal current densities and deposition durations were determined to obtain maximal deposit weights for different solutions and substrates. Deposits with thicknesses up to 10 μm were formed. The green deposits revealed a crystalline nature for compositions of x < 0.3, and an amorphous nature for x ≥ 0.3, independent of the substrate material. Voltage–electrolyte composition dependencies exhibited an ubiquitous minimum at x ≈ 0.3 to 0.4 independent of substrate type and deposition duration. These minima were attributed to the change in the electrical resistance of the deposit with composition and degree of crystallinity.
Similar content being viewed by others
References
J. A. SWITZER, Am. Ceram. Soc. Bull. 66 (1987) 1521.
L. GAL-OR, I. SILBERMAN and R. CHAIM, J. Electrochem. Soc. 138 (1991) 1939.
R. CHAIM, I. SILBERMAN and L. GAL-OR, ibid. 138 (1991) 1942.
K.-C. HO, ibid. 134 (1987) 52C.
S. B. ABOLMAALI and J. B. TALBOT, ibid. 140 (1993) 443.
P. BENDALE, S. VENIGALLA, J. R. AMBROSE, E. D. VERNIK Jr. and J. H. ADAIR, J. Am. Ceram. Soc. 76 (1993) 2619.
R. BACSA, P. RAVINDRANATHAN and J. P. DOUGHERTY, J. Mater. Res. 7 (1992) 423.
M. SHIRCHANZADEH, M. AZADEGAN, V. STAK and S. SCHREYER, Mater. Lett. 18 (1994) 211.
Y. MATSUMOTO, T. MORIKAWA, H. ADACHI and J. HOMBO, Mater. Res. Bull. 27 (1992) 1319.
Y. MATSUMOTO, H. ADACHI and J. HOMBO, J. Am. Ceram. Soc. 76 (1993) 769.
J. A. SWITZER, Nanostruct. Mater. 1 (1992) 43.
R. CHAIM, ibid. 1 (1992) 479.
R. CHAIM, G. STARK, L. GAL-OR and H. BESTGEN, J. Mater. Sci. Lett. 13 (1994) 487.
Idem., J. Mater. Sci. 29 (1994) 6241.
R. CHAIM, S. ALMALEH-ROCKMAN, L. GAL-OR and H. BESTGEN, J. Am. Ceram. Soc. 77 (1994) 3202.
E. ELSHEREEFY and M. F. R. FOUDA, J. Mater. Sci. Lett. 10 (1991) 299.
R. C. BRADT, J. Am. Ceram. Soc. 50 (1967) 54.
B. B. GHATE, W. C. SMITH, C. H. KIM, D. P. H. HASSELMAN and G. E. KANE, Am. Ceram. Soc. Bull. 54 (1975) 210.
I. ZHITOMIRSKY, L. GAL-OR and S. KLEIN, J. Mater. Sci. Lett. 14 (1995) 60.
I. ZHITOMIRSKY, L. GAL-OR, A. KOHN and H. W. HENNICKE, ibid. 14 (1995) 807.
E. M. LEVIN, C. R. ROBBINS and H. F. McMURDIE (eds.), “(American Phase Digramms for Ceramists”, Ceramic Society, Columbus, OH, 1979) p. 121.
M. RISTIC, S. POPOVIC and S. MUSIC, Mater. Lett. 16 (1993) 309.
L. INDIRA and P. V. KAMATH, J. Mater. Chem. 4 (1994) 1487.
L. INDIRA, M. DIXIT and P. V. KAMATH, J. Power Sources 52 (1994) 93.
D. B. GUNDEL, P. J. TAYLOR and F. E. WAWNER, J. Mater. Sci. 92 (1994) 1795.
R. CHAIM, I. ZHITOMIRSKY, L. GAL-OR and H. BESTGEN, J. Mater. Sci. 32 (1997) 389.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
ZHITOMIRSKY, I., CHAIM, R., GAL-OR, L. et al. Electrochemical Al2O3–Cr2O3 alloy coatings on non-oxide ceramic substrates. Journal of Materials Science 32, 5205–5213 (1997). https://doi.org/10.1023/A:1018690005679
Issue Date:
DOI: https://doi.org/10.1023/A:1018690005679