ISSN:
0044-2313
Schlagwort(e):
silicate solution
;
water glass
;
NMR spectroscopy
;
dre adsorption
;
Chemistry
;
Inorganic Chemistry
Quelle:
Wiley InterScience Backfile Collection 1832-2000
Thema:
Chemie und Pharmazie
Beschreibung / Inhaltsverzeichnis:
The Influence of Temperature and Impurities Addition on the Properties and the Constitution of Sodium Water Glass SolutionsSodium water glass (NaWG-)solutions of constant composition (SiO2/Na2O = 3,3; CSiO2 = 6,2 M) and different concentration of impurities (Fe, Al, Ti, Cu, chloride, sulfate) were investigated in dependence on temperature by means of the dye absorption method, 1H- and 23Na-NMR spectroscopy. It is shown, that the differences in the dye absorption spectra of normalized technical NaWG-solutions, mainly depend on the Fe-concentration in the solutions and their thermal history. From the results follow a crosslinking of polymeric silicate species by Fe—O—Si bonds and/or hydrogen bridges and a fully or partially degradation of these bonds at higher temperatures (150°C).
Notizen:
Natriumwasserglas-(NaWG-)lösungen konstanter Zusammensetzung (SiO2/Na2O = 3,3; CSio2 = 6,2 M) und mit unterschiedlichen Fremdatomgehalten (Fe, Al, Ti, Cu, Chlorid, Sulfat) wurden in Abhängigkeit ihrer thermischen Vorbehandlung mit Hilfe der Farbstoffadsorptionsmethode sowie der 1H- und 23Na-NMR-Spektroskopie untersucht. Es zeigt sich, daß die Unterschiede in den Farbstoffspektren normierter technischer NaWG-Lösungen im wesentlichen von dem Fe-Gehalt der Lösungen und ihrer „thermischen Vergangenheit“ abhängen. Die Ergebnisse der Farbstoffmethode und NMR deuten darauf hin, daß in Fe-haltigen NaWG-Lösungen bei 80°C Vernetzungen der polymeren Silicatteilchen über Fe—O—Si-Bindungen und/oder Wasserstoffbrückenbindungen erfolgen, die bei höheren Temperaturen (150°C) wieder ganz oder teilweise gelöst werden.
Zusätzliches Material:
5 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/zaac.19926140817
Permalink